Electronics Forum | Thu Jul 15 13:27:42 EDT 2010 | xps
Thanks... anyway I confirm, the nickel disappear (verified by cross section)and a strange substance greyish above gold, covering the tabs after test. I don't know the reason for this phenomenon. I don't believe that with proper electrolytic nickel fi
Electronics Forum | Thu Apr 07 02:38:20 EDT 2011 | aungthura
I didn't know the difference for BGA. We found solderability probelm as show in attach.Then, we called to PCB maker and they said that it could be caused because of PCB finishing. Do you agree this probelm was happend because of PCB finishing? Unfor
Electronics Forum | Mon Aug 16 20:32:10 EDT 2004 | davef
First, we didn't say "electrolytic soft gold with a minimum thickness of 5-8 of Au". We said, "'electrolytic soft gold' thickness 5 to 8uin". FOCUS. ;-) Second, we're unaware of an industry accepted specification that you can reference. IPC-2221
Electronics Forum | Mon Aug 16 16:37:08 EDT 2004 | davef
As we mentioned in an earlier response in this thread [Q5], you do NOT want to solder to hard gold. Hard gold is a wear surface. [That's IT, that's the LIST.] If you want to solder to gold, then either use: * IPC-4552 ENIG specification, mentioned
Electronics Forum | Wed Aug 11 18:36:03 EDT 2004 | davef
90 Knoop. Q2: Thickness is 4 to 10 u" for Au and 300 to 400 u" for nickel A2: This looks like a ENIG spec. Although, the Ni is quite heavy, 150 uin is sufficient for most applications. [IPC-4552 ENIG specification: * Gold thickness of 0.075 - 0.125
Electronics Forum | Fri Aug 17 11:55:31 EDT 2001 | davef
5uin. Your nickel thickness is fine. Although if you wanted to trade costs, consider giving-up nickel to 150uin thickness, while increasing the gold thickness. Gold over electroless nickel creates brittle joints because of phosphorous in the nicke
Electronics Forum | Tue Feb 21 01:32:49 EST 2017 | soldertraining
Looking for advice on soldering lead free paste to a board with very heavy gold plating, In my opinion, Gold contact surfaces are often used on circuit boards with membrane switches which is a choice of technology for industrial, commercial and consu
Electronics Forum | Wed Apr 21 17:08:32 EDT 2004 | dave
Congratulations on your new customer. This could be a keeper. Here's what you're familiar with: Electroless Nickel - per MIL-C-26074 and ASTM-B733. Electroless nickel describes the plating of nickel deposits, which may contain phosphorus and boro
Electronics Forum | Wed Dec 14 07:34:33 EST 2005 | davef
Mike Ozzy If I came to your house, I wouldn't punch you. I'd make you buy me beer. Vern Solberg; Tessera Technologies Inc., 3099 Orchard Dr, San Jose, CA 95134; 408 568 3734 F408 894 0768 vsolberg at tessera dot com. If that doesn't work try: Tes
Electronics Forum | Fri Mar 24 18:07:25 EST 2006 | Chris
Flash gold is just thin gold plating over electroless nickel or electrolytic nickel. Flash gold is electrolytic gold where the panel is connected to a plating rectifier and current causes the plating process to occur. Gold thickness is controlled b
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830