Electronics Forum | Fri Aug 14 09:40:59 EDT 2015 | jvalverde
Hello, I want to make a simple conformal coating machine, I think in a Cartesian robot with MACH3 software. My questions are about the G-Code for the program (the software to design: % open/close nozzle, the paths (trajectory), import the pcb fi
Electronics Forum | Thu Jul 03 17:29:42 EDT 2008 | mikesewell
Re: item 3 - there are ultrasonic thickness machines (Panametrics makes one) that can measure coating dry with a small transducer head. A little pricey for ones that measure reliably in the .003" +/- .002" range.
Electronics Forum | Wed Mar 04 10:59:24 EST 2015 | jpierre
Hi first DS65 version is a specific dilution for dispensing machine, in this case the typical process is following: application of the conformal coating extraction of solvent (low extraction power is better)2minutes and drying the drying can be done
Electronics Forum | Thu Sep 20 03:31:42 EDT 2018 | minhhaioh34
Hi all, I need some pro help me with issue bubbles after coating. some information for some pro: Machine: Asymtek Chemical: Achime AVR80 Oven: IA 4 zoon4 ( setting 100 100 90 80 conveyor speed: 0.6 m/min). I had happened before and after the oven. W
Electronics Forum | Thu Nov 01 12:52:18 EDT 2018 | emeto
Thanks Rob, It looks like my customer wouldn't let me to change the material. However, this potting material still sticks to the non sticking fixture that I have. Can anyone give me a non sticking material that I can make these fixtures out of?
Electronics Forum | Tue Oct 16 10:06:41 EDT 2018 | emeto
Hello experts, I have an assembly that goes through pretty tough sterilization on regular basis. Currently I am using a two component material in potting process. I was wondering if you can help me with material that can handle high temp and humidit
Electronics Forum | Wed May 08 14:24:22 EDT 2013 | wahahasteven
we are using acrylic conformal coating on the PCB. Under the same program, same parameters (not changing anything on the machine), and we always found one or two boards have some spots which are not coated (shown as picture). The location of the spot
Electronics Forum | Thu May 09 10:12:08 EDT 2013 | wahahasteven
this is one of my project. I have tried to remove coating only on those areas with alcohol and thinner, then program the machine to coat the removed area again. But the result obviously shows that two different tones of coating on the board. I also
Electronics Forum | Mon May 16 18:03:30 EDT 2005 | davef
Key Issue: Will this machine solder your boards? You never know until you solder one. Any other avenues of analysis involve substantial risk. Flux Selection * High or low solids * VOC or VOC-free Solder Alloy * If using lead-free, avoid stainles
Electronics Forum | Tue Jul 30 17:45:56 EDT 2002 | davef
What's this 'metalic coating on both sides'? Is that like a 'two-sided board'? I expect that your 200�F is the primary side temperature just prior to entering the wave. If not, you need more juice [depending on your flux and all that]. [Some mode
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830