Electronics Forum | Tue Oct 17 12:07:58 EDT 2006 | pms
ya don't need no stinkin pads. just run sum fine gauge insulated jumpah wires from da I.C. legs (da ones with da missin pads) to da traces or where-ever dem traces end up. dat should get er dun !!!!
Electronics Forum | Wed Oct 18 07:51:14 EDT 2006 | davef
Look here: http://www.circuittechctr.com/ As a low cost approach, use copper foil purchased from a stained glass window hobbyist shop. Cut foil pieces to size with a sharp knife. Epoxy the pieces in place of the damaged pads. Tin and then solder th
Electronics Forum | Mon Oct 16 17:46:49 EDT 2006 | Dan
Recently I was given a bad Bios Link from Toshiba which fried my Bios and now my laptop boots to a black screen. I recently unsoldered and removed the existing Bios chip and have ordered anotherfor replacement. Unfortunately while removing, i damag
Electronics Forum | Wed Jul 01 13:17:39 EDT 2015 | davef
Cheryl Tulkoff and Randy Schueller do a good job summarizing the thinks on pad cratering here: http://www.smta.org/chapters/files/uppermidwest_padcratering.pdf Potential Mitigations to Pad Cratering * Board Redesign * Solder mask defined vs. non-s
Electronics Forum | Thu Sep 10 15:06:11 EDT 2009 | dyoungquist
My guess is that he is talking about the gold plated pads not fully wetting with solder. We have seen this on some of our ENIG boards with the gold still showing at the far corners of the rectangular pads. Not knowing if this is hand soldering or p
Electronics Forum | Fri Jun 14 14:30:36 EDT 2002 | davef
Assuming you are talking about solderable surfaces: People specify various materials to protect the solderability of the pads on the board. Gold, actually, Electroless Nickel - Immersion Gold [ENIG], is popular. * Board fabricators like it because
Electronics Forum | Wed Aug 22 21:42:54 EDT 2007 | davef
Questions are: * Do these pads take solder? How well? * Have you stripped the gold and evaluated the condition of the nickel?
Electronics Forum | Mon Aug 27 08:03:32 EDT 2007 | davef
Actually, you will be soldering and wire bonding to the palladium layer, so we should have asked if you checked that layer, rather than the nickel. We not sure of the source of the copper that your see on EDX. It's possible copper from the pad migra
Electronics Forum | Thu Aug 23 09:52:38 EDT 2007 | d0min0
Hi, in past we had an issue with ENIG surface, black was Ni that get pass the Au - but it was discovered after reflow (SnPb) and the IC was losing contact with Cu tracks...at customers application :| Reason was as I remember too thin Au sufrace... w
Electronics Forum | Sun Aug 26 11:27:12 EDT 2007 | vangogh
Hi Davef, Thanks for the reply. There seem to be no issues on SMT reflow based on some samples done. We have not stripped the gold yet. We did a X-section+EDX and we are seeing traces of copper on the nickel layer. Any idea what is the implication of
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830