Electronics Forum | Mon Aug 03 17:15:56 EDT 2020 | rgduval
In general, no. If you've got the right BGA rework equipment, you should be able to locally heat the part area that you're reworking. Though, if you're finding defects related to thermal stress, it might not be a bad idea to pre-heat the rest of th
Electronics Forum | Mon Mar 13 08:46:49 EST 2006 | geocominc
Yes, All six new (LF ready kit) thermocouples are tested good.I would like to say boards are populated on both side back to back with two heavy PLCC's side by side just like having heatsinks and ground plane.Some Odd design.Next try will be to have a
Electronics Forum | Fri Jul 31 15:04:49 EDT 2020 | mvargas
Hi To perform a BGA repair of a 0402 size component, on a 23" x 18" board, is it necessary to preheat the entire board or only the area where it will be repaired? Thanks!
Electronics Forum | Wed Jul 29 07:26:12 EDT 2009 | dilogic
Hi Patrick, thanks for the response. I might add some more information - we succesfully soldered some boards with the same settings of belt speed, pre-heat temp. etc. This batch of boards differs from the previous in a way that they are 4-layer. May
Electronics Forum | Thu Mar 04 10:21:55 EST 1999 | Igmar
Can someone please advise me to the rework procedure for removal and replacing Ceramic Chip Capacitors (e.g. 0805, 1206, etc.)? Is it necessary to pre-heat ceramic capacitors before soldering them onto a PCB with a soldering iron? Is this just a rec
Electronics Forum | Mon Mar 08 16:23:24 EST 1999 | Dave F
| Can someone please advise me to the rework procedure for removal and replacing Ceramic Chip Capacitors (e.g. 0805, 1206, etc.)? | | Is it necessary to pre-heat ceramic capacitors before soldering them onto a PCB with a soldering iron? Is this just
Electronics Forum | Thu Aug 04 16:34:03 EDT 2005 | bhu
You haven't mentioned whether you are producting only through hole product or if it is mixed technology. What kind of flux (no clean, H2O clean) you are using and whether you performed a first article at part stuffing prior to wave. Generally, you
Electronics Forum | Tue Aug 29 11:22:12 EDT 2006 | yuceltemel
Dear Bruce, We had the same problem in the same condition. Every compnent and the PCB (OSP) has changed as lead-free and we need to solder them with SnPb. For solution we have increased the flux amount applied on PCB and the pre heat zone temper
Electronics Forum | Sat Jan 19 02:29:11 EST 2002 | ianchan
Thanks for the tips... found out the ex-employee guy, had pre-bake conditioning put into the process flow, as this pcb is made of polymide material, that is reputed to have historical patterns in thermal sensitivity. To avoid "thermal damaging" the
Electronics Forum | Sat Apr 30 13:56:31 EDT 2005 | steve
My experience with different size boards and pre-heaters. The perfect world (right?) you would saturate the complete pcb with bottom pre-heat. But it is difficult with repair and rework equipment, not to mention the expense and foot print of large pr
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830
.gif)