Electronics Forum | Sun Dec 08 22:20:39 EST 2002 | grantp
Hi, We have been manufacturing a PCB, however it's been quite tricky to profile, as the edges of the PCB are reflowing before the center of the PCB. I have looked at the design, and there is a small power plane for 2.5 Volt in the center of the PCB
Electronics Forum | Fri Jan 03 02:03:58 EST 2020 | sssamw
What's your target for voiding? I cannot see it violate 25% of solder joint area. Process setting and PCB design can impact the voiding, many factors, such as PCB pad, stencil aperture and thickness, re-flow profile, solder paste, etc.
Electronics Forum | Tue Aug 10 14:50:59 EDT 2004 | C Lampron
Snehal, Look at the spec sheet for the paper phenoline PCB. Look at the max temp. If it is at or lower than 183 degrees C, here lies the problem. If it will withstand higher temps at a shorter durration, you can possibly speed up the belt but like D
Electronics Forum | Wed Feb 10 18:17:46 EST 1999 | Earl Moon
| Hi, | | Has anyone found any significant differences on profiling using populated and unpopulated boards? Is it worth sacrificing a board to the profile gods? | | Joe | What's the cost of not doing it. In the same breath, why not wait for a sc
Electronics Forum | Sat Apr 10 11:47:16 EDT 2004 | mskler
Hi all, When we are producing A gold Plated PCB Then the Prob Of Dry soldering is coming Profile temps are 130, 150, 180,and 220 top & 215 bottom.Then what are the other causes or Precautions may be taken.
Electronics Forum | Fri Aug 27 00:26:14 EDT 2004 | charly
hi, encounter few cases PCB was delam after reflow, and the supplier was refuse that this is a PCB manufacturing defect as the fallout is low within one lot. the cost for this scrap is high after PCBA level, my query here are 1) is there any way
Electronics Forum | Mon Nov 27 22:01:57 EST 2023 | emeto
It is about thermal mass and heat dissipation. If you want to be accurate, you should profile each one. If you want to be efficient, You should design all panels to come to the same size. This way variation from panel to panel will be minimal (given
Electronics Forum | Wed Mar 26 16:12:46 EDT 2008 | jlawson
If you have jobs where you can not, there is a company in Japan that makes the best v-groove depanelers called TST, 'guru's in v-groove depanelising'. Their systems can be supplied to reduce stress on cutting to near zero compared to CAB and other lo
Electronics Forum | Fri Aug 24 01:25:58 EDT 2018 | cupet
Hi everybody, please advise in case of soldering problems after the reflow soldering. The problem occurs randomly at different locations on different PCB's (not the complete surface of the board). These places are very difficult for rework. Could you
Electronics Forum | Wed Jul 18 11:41:35 EDT 2018 | stephendo
I have only seen ceramic PCBs a couple of times. Make sure you run a temperature profile on a PCB. But you should do that anyway. Other than that I don't remember any other issues. I can't remember how they were panelized You might want to check into
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830