Electronics Forum | Thu Jul 23 11:39:16 EDT 1998 | Russ Miculich
Are you using a HASL board or an organic protection on the pads? This will help determine as to whether paste is necessary or just a very active/tacky flux should be used. Tight process control will also help in the reflow oven. Many users don't wan
Electronics Forum | Fri Feb 23 10:10:32 EST 2024 | emanuel
Well, the story is a little more complicated. The product is also an LED lamp made on an aluminum PCB with the LEDs on one side and the drivers on the other. The board itself is not big, about 90x90mm and most of the components are soldering well. Us
Electronics Forum | Wed May 11 13:27:30 EDT 2005 | Sam Ho
i want to know which type of solder paste and reflow profile can support the solder pad with nickel but not covered gold on the pcb.
Electronics Forum | Mon Jun 18 17:41:07 EDT 2001 | genny
Hi, I put this on the technet forum, and I know some of the same people are here, but I thought I might catch others here as well. We have PCB's which are populated at the CM level with no-clean solder paste. However in house we use a solder wire s
Electronics Forum | Sun Jul 29 23:58:08 EDT 2001 | Frank
Hi Dave Thanks for your information. The problem that I found is paste not stick well on pads ( solder paste printing process). When the table move down (PCB saperate from stencil) some of paste stick on aperture instead pads. Solder paste : Delta
Electronics Forum | Sat Jul 28 03:05:35 EDT 2001 | Frank
Hi guy Does anyone have experiance with printing problem between solder paste water soluble 62/36/2 and gold plating PCB? I do have problem about insufficient solder after printing although I used the same printing parameter as when I print with ano
Electronics Forum | Tue Feb 03 03:35:30 EST 2009 | sachu_70
Hi Jose, such a process is possible, but you need to confirm that the PCB material has high Tg. In additon, you need to re-look solder paste printing parameters and make required changes in stencil apperture design for optimum solder volume. Just a
Electronics Forum | Sun Feb 01 07:50:07 EST 2009 | davef
The concern about lead contamination of lead-free solder has to with zone refining. For more, look here: http://www.smtnet.com/forums/Index.cfm?CFApp=1&Message_ID=30315
Electronics Forum | Sun Jul 29 08:36:39 EDT 2001 | davef
You have provided very little information. Two similar possibilites come to mind: poor pad solderability protection and old boards. POOR SOLDERABILITY PROTECTION: Maybe the nickel plating under the gold is oxidized, contaminated, or otherwise very
Electronics Forum | Mon Jul 30 21:12:32 EDT 2001 | davef
"Poor release" (paste hanging-up in the stencil holes) could have three main (or combination of) causes: 1 Equipment: Stencil is too thick. Specifically, a 6 thou stencil should be OK, providing you don�t violate the area and aspect ratios in the fi
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830