Electronics Forum | Fri Jul 11 10:00:05 EDT 2003 | davef
Component manufacturers recommend limits on the power and period of ultrasonic cleaning. Examples are: * PRECAUTIONS AND GUIDELINES MULTILAYER CERAMIC CAPACITORS: (9) Ultrasonic cleaning time shall be ten minutes maximum. When the power of ultrasoni
Electronics Forum | Wed Jun 23 13:34:29 EDT 2004 | df_indy
I am four weeks into my new job, there always seems to be some issues here with PCB every week. Today while I was checking some assemblies with micro-scope, I found a lot of tiny bubbles/blisters on the board. They are just little dots if you look
Electronics Forum | Mon Aug 09 04:15:33 EDT 1999 | Jacqueline Coia
I am having cleaning problems when processing PCB's which have TAIYO solder mask on them. After processing, hand soldering and cleaning, a sticky residue is remains, resulting in a cosmetically poor finish with tide marks etc. Other soldermasks do no
Electronics Forum | Thu Apr 09 06:28:11 EDT 2009 | qualityguy
We have different Solder mask 'gloss' and 'satin' the gloss has a surface energy =40 dynes. The test evidence to date is strong correlation between surface energy, mask type, HASS failure
Electronics Forum | Sun Apr 05 12:30:22 EDT 2009 | qualityguy
Forum: Has anyone experience conformal coat peeling after HASS and the failure mechanism being low surface energy attributed to the solder mask?
Electronics Forum | Tue Apr 07 15:36:15 EDT 2009 | gtemkin
Most of the conformal coating manufacturers recommend verifying the compatibility of their coating with the solder mask, so it's no surprise that occassionally there will be such issues. Are you sure your conformal coat is completely cured? If your
Electronics Forum | Fri Apr 10 07:52:16 EDT 2009 | davef
On cure checking, we have this undated note from Jack Crawford at IPC * IPC-SM-840C "Qualification and Performance of Permanent Solder Mask" has several Test Methods for different types of solder resist material, but probably the only applicable one
Electronics Forum | Wed Nov 20 01:38:53 EST 2019 | ajspec
Hi, i'm facing solder mask peel off but limited to the solder defined pad only(opening area). no peel off on the other area and it happened on electroless nickel immersion gold finishing only. for other finishing is not affected. kindly advise if you
Electronics Forum | Wed Dec 11 11:26:25 EST 2019 | SMTA-Norah
Yes, a polite complaint to our board shop later and the next batch didn't have that problem at least. I'm not convinced it's an ENIG issue as there was variability panel to panel in the first place.
Electronics Forum | Tue Dec 10 13:35:34 EST 2019 | scotceltic
I am looking to see what people are using for a min-max range to supply your PCB fabricators regarding solder mask thickness. I saw some points in the archives but not too much regarding what people are providing as their spec ? Any help would be a
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830
.gif)