Electronics Forum | Wed Feb 02 21:17:55 EST 2000 | Steve Harshbarger
Istvan, The advise from both Roni and Mike sounds right on the money. The problem is most likely that your PCB is not completely dry (the flux has not completely evaporated) in the area where these solder balls occur. You have a number of differen
Electronics Forum | Thu Aug 28 11:02:28 EDT 2008 | omid_juve
we have two similar pcb from two different pcb manufacturer one of them passed the wave soldering without any short circuit and residue and another one passed it with many residue . don`t you think that the type of solder mask from these two pcb manu
Electronics Forum | Wed Jul 03 14:08:10 EDT 2002 | gbriceno
I' designing a PCB with SMD components to optimize the land patterns for wave soldering. I find that the IPC-SM-782 land patterns are not robust enough for wave soldering, yielding ramdom skips and bridges. This PCB will also give me insight on sha
Electronics Forum | Thu Aug 05 17:29:24 EDT 2004 | russ
what type of flux are you using and what type of solder resist is on the PCB solder resist (Gloss or Matte), also what is the orientation of the connector to the wave flow and what is the pitch of the leads? Russ
Electronics Forum | Fri Nov 09 04:15:25 EST 2007 | reypal
how about applying solder resist on the area where you have bridging occurs..you may ask your pcb supplier the possibility.
Electronics Forum | Fri Dec 16 03:47:46 EST 2005 | gpaelmo
Anyone have problems wave soldering white tin finish? We are an ems and our customer provides us the pcb's. SMT and TH components on the board. SMT is fine but when we wave solder, wetting to top side is very poor (solder only flows half way up). We
Electronics Forum | Thu Aug 12 08:03:54 EDT 2004 | Rafal M.
We used fluxes: Cobar 94-QMB (no bismuth), RF800, Cobar94RXZ-M, with foam and spray fluxers: MBO clean alloy SN63PB37.experienced with changing preheatting, speed of covoyer single and double wave., we tried every combination. I think the problem is
Electronics Forum | Wed Aug 27 14:58:21 EDT 2008 | omid_juve
we have problem in setting the density of a no clean flux for using before wave soldering . first we dilute the flux but we have many short circuit problem between the pads of edge connector,then we densify the flux all the short circuit is removed b
Electronics Forum | Mon Aug 16 04:55:30 EDT 2004 | roel
Concerning the solder-balls, there are a few causes for this. Try to slow down your solder-speed (P.e 80cm/min). Can you measure temperature after the pre-heat zone? Are there also blow-holes in the joints? Personally I think there is some water in t
Electronics Forum | Mon Nov 05 00:51:58 EST 2007 | omidjuve
We have a problem with soldering of a 96 pin header connector(9001-11961c00l1a from kingmate) we use 3 different wave soldering but in all of the machines we have many short circuit between the pins . the wave soldering machines that we use is fr
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830
winsouce.jpg)