Electronics Forum | Tue Aug 16 11:27:14 EDT 2005 | saragorcos
Hi Peter, I posted these links to Technet as well, but figured I would add them here as well in case any of the smtnet readers would like to see them. Here are some links to some articles about white residue sources, and whether or not white residue
Electronics Forum | Wed Mar 12 11:41:41 EDT 2008 | gregoryyork
Blimey just seen the picture that is bad. You could try to dissolve some of the residue/gunge in IPA if it is flux residue it should readily dissolve if it is resist issue then only portions will dissolve leaving a white powder which is Talc If you
Electronics Forum | Mon Dec 06 15:24:46 EST 1999 | C.K.
I suggest that your customer is living in a land of washable >fluxes and has not kept currect with the vagaries of no-cleans >and your mission is to educate them of: >1 Costs of washing a no-clean and then trying to remove the >white residue >2 Ac
Electronics Forum | Fri Jul 19 21:19:25 EDT 2002 | yngwie
Hi, I know this is a total screwed-up. Operator used the wrong paste. It was supposed to be a clean paste but she was issued with no clean paste. What happen was when the brd processed thru', after the reflow, the girl passed the boards thru' DI wa
Electronics Forum | Sat Jul 20 09:02:04 EDT 2002 | davef
Probably 2) what is this white residue material (chemically )? => Natural or synthetic rosin 3) Can Saponifier wash, helps? If not what is the best solution to remedy this white residue. => Probably a saponifier will work. Some NC flux residues
Electronics Forum | Tue Aug 16 00:27:12 EDT 2005 | Peter
Hello, I have a question on white residues formation at wave soldering. We have recently run experiments to test the performance of various halide-free water soluble fluxes (ORH0 under JSTD-004). The flux was applied through a spray fluxer and all P
Electronics Forum | Mon May 26 08:59:32 EDT 2008 | davef
It's possible that the flux residues from the solder paste used in your SMT process is not compatible with your water wash process. For instance, some no-clean fluxes leave resudues that are not water washable. When these residues are washed, they de
Electronics Forum | Mon Apr 29 10:42:47 EDT 2002 | Jim M.
I had problems with white residues on both WS609 and WS 3060.The WS 3060 turned out to be a carbonized material.The composition after analysis (Energy Dispersive X-ray spectrum) turned out to be tin,tin,phosphore and cloline and tin. Alpha also have
Electronics Forum | Mon May 26 11:02:17 EDT 2008 | jandon
Hi Mr. Necdet Ozyonum, Recently we did have same kind of problems when we use lead free reflow profile for leaded solder paste (AIM WS-483). There where solder resist lacks, we found white residue after aqueous cleaning. Not in the solder joints but