Electronics Forum | Tue Feb 03 03:35:30 EST 2009 | sachu_70
Hi Jose, such a process is possible, but you need to confirm that the PCB material has high Tg. In additon, you need to re-look solder paste printing parameters and make required changes in stencil apperture design for optimum solder volume. Just a
Electronics Forum | Sun Sep 10 18:54:12 EDT 2000 | Craig
Does anybody do this? Are there any problems with doing this? Thanks Craig
Electronics Forum | Thu Oct 31 15:36:20 EDT 2013 | ke6zoy
Thanks Pete!
Electronics Forum | Fri Jan 30 15:11:50 EST 2009 | joseluis_amper
Dear Sir. Recently we had a problem in our production. We had pcbs with no RoHs (with solder Pb in pads) but we used paste Lead Free. I want to know if we will have problems in this solders in the future, because (perhaps)the solder will be broken, o
Electronics Forum | Thu Oct 31 11:54:10 EDT 2013 | ke6zoy
I work in a leaded paste world due to aerospace environmental requirements. There are a few cases where parts are only available from suppliers as RoHS. Can anyone recommend how to process these into a leaded assembly? Is it just reflowing at a hi
Electronics Forum | Mon Sep 11 16:11:50 EDT 2000 | John Thorup
Hello Craig In a nutshell - bad idea Please check the achives as this has come up a number of times John Thorup
Electronics Forum | Sun Feb 01 07:50:07 EST 2009 | davef
The concern about lead contamination of lead-free solder has to with zone refining. For more, look here: http://www.smtnet.com/forums/Index.cfm?CFApp=1&Message_ID=30315
Electronics Forum | Fri Jan 30 18:24:09 EST 2009 | gsala
Buenas dias Jos�, It shoul not be a problem. We had situation like that when in the early 2006 the Lead Free fase in Pb fase out, no pbm on solder joints. Today, after about 3 years, those cards are stil working in the field without any defect. Reg
Electronics Forum | Tue Feb 03 10:25:56 EST 2009 | milroy
Hi What is the surface finish you have? Following are true if you have HASL-LeadFree surface. I have had the same problem 3years ago and we did some micro-sectioning for further analysis, still the boards are functioning properly. But you have to
Electronics Forum | Thu Oct 31 12:33:14 EDT 2013 | pbarton
You should have no difficulty with QFN or QFP parts when using non-RoHS solder. The QFP's are most likely to have tin plated leads and the metallisation on the QFN lands the same, or ENIG. Check the component part datasheets to verify the plating an