Electronics Forum | Thu Dec 29 10:47:05 EST 2005 | Chris
The paper Dave posted the link for is great. I have to go back and read it in depth. I can build prototypes by wirebonding to ENIG. I can do it on a manual wirebonder but I don't have the patience to do it on a magazine to magazine automatic machi
Electronics Forum | Wed Dec 28 16:03:53 EST 2005 | Chris
I have lots of experience with thermosonic gold ball bonding. You can read the literature and you will probably find some papers that say you can do it. I have never been able to do it. We gold ball bond all day long with little problems at all bu
Electronics Forum | Tue Sep 10 10:42:36 EDT 2013 | capse
Plasma cleaning is used extensively to clean surfaces prior to wire bonding.
Electronics Forum | Sat Mar 15 20:24:13 EST 2003 | ramanandkini
Thanks Mr.Dave. Sorry for the delay. One of our major prolems in ENIG plated surface is that wire does not stick. For many years we were getting a bond strength of 14 grams in both ENIG and electroplated surfaces. Now one vendor supplies ENIG boards
Electronics Forum | Mon Sep 09 15:38:02 EDT 2013 | arendonk
Hi, We are having issues aluminum wirebonding on ENEPIG plated PCB by a too low pull force and or having lifts (1% range). Could any body advice how to solve this problem? Is there a special wire bond grade required? How to best clean contaminant
Electronics Forum | Thu Oct 05 07:23:34 EDT 2006 | Chris
Hi all experts, I have no background about PCB or SMT process. I am now encountering some issues after SMT - Unstable stitch bonding condition. I am now suspecting some contaminants remain on lead after cleaning. Therefore, how can I check th
Electronics Forum | Tue Jul 01 17:38:24 EDT 2003 | jartman
I've faced this several times in the past, and the only real solution is to wirebond before SMT assembly. Everything leaves a residue, and trying to clean a residue off later is basically hopeless. This may require some trickery in your SMT process
Electronics Forum | Wed Jan 09 17:14:48 EST 2002 | mregalia
Do you bond with Al or gold wire? What happens if the Ni is over 150 microinches? Thickness of nickel is one those things that we have not been consistent with. The industry seems to pretty much universally call for 100-200 microinches. Our old board
Electronics Forum | Mon Aug 02 11:21:29 EDT 2004 | sforman1
Use MicroCoat Technologies UV cure solder mask. will leave PCB absolutely clean. used in many PCB solder/wirebonding apps. http://www.m-coat.com
Electronics Forum | Thu Nov 03 07:43:52 EST 2005 | davef
Questions are: * Is the problem 'wire bonds that don't stick' or 'wire bonds that fall or break off later'? * What materials are you working with? * What is your working time after plasma clean? * What does surface analysis tell you about surface con
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830