Electronics Forum | Thu Nov 03 02:34:46 EST 2005 | Rosewood
We've recently encountered some problems with wire bond strengths. I'm looking for anybody that has had some experience with different types of substrate contamination and methods for cleaning. There is no visible contamination on the gold pads, bu
Electronics Forum | Sat Oct 02 03:51:28 EDT 1999 | Brian
| | Can someone suggest what material I have to use to protect components by electrical discharge on ptfe based boards? | | It should have high resistivity, thermal stability (-40 +70 'C),perfect adherence on ptfe... | | Many tahnks | | | Don't kno
Electronics Forum | Mon Oct 04 04:37:57 EDT 1999 | Gian.D
| | | Can someone suggest what material I have to use to protect components by electrical discharge on ptfe based boards? | | | It should have high resistivity, thermal stability (-40 +70 'C),perfect adherence on ptfe... | | | Many tahnks | | | | |
Electronics Forum | Fri Oct 13 17:21:05 EDT 2000 | Jason Nipper
A few weeks back we experienced a wave process problem where we received deposits on our pcb. At first we though it was dedrites but after an outside analysis of the deposits they were found to be tin. We have tried to remove the deposits with brus
Electronics Forum | Wed Oct 19 07:44:33 EDT 2005 | davef
When a hole is drilled during board fabrication, it can transfer resin from the base material (eg, FR4 core or prepreg) to cover the exposed edge of conductive material in the wall of a drilled hole. This is called resin smear. Etchback is a control
Electronics Forum | Thu Jul 22 21:26:29 EDT 2004 | Grant
Hi, It's removed from the fridge, and the tube is loaded into the stencil printer, however it's winter here right now, so it's still quite cold. It's Australia, so when I say cold, that's relative, however the room can be about 10 dec C in the morni
Electronics Forum | Wed Oct 06 08:49:36 EDT 1999 | Dave F
| | | | Can someone suggest what material I have to use to protect components by electrical discharge on ptfe based boards? | | | | It should have high resistivity, thermal stability (-40 +70 'C),perfect adherence on ptfe... | | | | Many tahnks | |
Electronics Forum | Wed Oct 18 10:02:04 EDT 2000 | Jason Nipper
I know it's a tin residue because we have a Cheme in house who had a spectrum analysis performed in an outside lab. The waves parameters were out of control long enough to effect a number of units that are, we�ll can I say substaincial in a fiscal s
Electronics Forum | Mon Oct 16 20:29:32 EDT 2000 | Dave F
Jason: How did you determine that the deposits are tin oxide? What does this stuff look like? Klein Wassink "Soldering in Electronics" (p. 221, quoting original work by others). States (in effect) tin (or solder) quickly forms a protective oxide