Electronics Forum | Tue May 23 09:50:37 EDT 2006 | flipit
They work well in silver conductive epoxy in hybrid applications. They are very poor in no clean applications. They don't work that well in OA solder paste either. Used them once in OA paste and in a nitrogen. They looked just fine. Solder to Pd
Electronics Forum | Tue Jul 30 08:37:39 EDT 2002 | davef
When you talk about 'poor wetting', 'dewett', 'no wets', etc.; are you seeing solder pulling back or away from the pad? Please describe the condition. Dewetting. The condition in the solder joint in which the liquid solder has not adhered intimate
Electronics Forum | Tue Feb 21 09:19:50 EST 2006 | Chunks
Hi Mark, Not to be condescending, but is your 265 camera in focus? I've seen one instance of this. If it�s not the camera, and you are sure all your other parameters are good, , then poor definition can be from bad snap-off or bad gasketing. Snap
Electronics Forum | Tue Jul 30 10:04:51 EDT 2002 | dason_c
Dave, I am very interesting to know about the dewetting or pull back, we are currently use the uP78 paste. Will nitrogen, profile setting help to reduce the dewetting. Thank.
Electronics Forum | Mon Feb 20 20:47:59 EST 2006 | davef
We assume your stencil is clean. So, try: * Reduce stencil separation speed. * Reduce squeegee pressure. If the pressure is not proper, excess number of particles are stuffed into an aperture and inner pressure / friction among particles increase, an
Electronics Forum | Tue Jul 30 17:47:50 EDT 2002 | davef
Dewetting: Solder does not adhere to lead or land, caused by: * Poor solderability of lands. * Poor solderability of leads. * Solder paste integrity. * Lead plating integrity. Need more information, please: * What is dewetting [ie, component, pad, e
Electronics Forum | Tue May 23 09:36:11 EDT 2006 | Steve
Not being funny here but I understand exactly what you are saying and sounds exactly the same as we experienced. Seriously try a different paste. Give Tamura a ring and I am sure they will give you a sample. I don't have the exact part code but they
Electronics Forum | Mon Jul 29 16:43:55 EDT 2002 | mcm4me
I have a customer with up to 8% scrap from one board supplier and 1% from another supplier for solder dewett and no wet over ENIG finish with mask defined pads. Initially I suspected mask residue on pads because of the no wets but I have come to find
Electronics Forum | Tue Jul 30 12:15:15 EDT 2002 | Rick Lathrop
Hi Dave, The paste applied to the board ends up on the tombstone. The pad has a thin covering of solder most of the time, this is why I think they call it a dewet. Occasionally the pad shows some areas of gold and very rarely are some pads not wet at
Electronics Forum | Mon May 22 18:19:29 EDT 2006 | Steve
I have read some threads about poor wetting on palladium-silver (Pd-Ag) coated components. I followed the suggestions, but I am still having a problem. The part is an 0603 chip type (Vishay varistor). The Process: solder paste is lead-free Alpha Met