Electronics Forum | Tue Jul 30 08:37:39 EDT 2002 | davef
When you talk about 'poor wetting', 'dewett', 'no wets', etc.; are you seeing solder pulling back or away from the pad? Please describe the condition. Dewetting. The condition in the solder joint in which the liquid solder has not adhered intimate
Electronics Forum | Wed Jul 10 22:32:46 EDT 2002 | redmary
i just find the gap inside the component from the cross-section, it indeed exists the interal crack, not solder joint crack. but why the failed capacitor is well after some time. and the other suspicion is the quality of the component.
Electronics Forum | Tue Jan 15 09:42:40 EST 2002 | davef
Here's two choices. 1 Before accepting a lot of boards from your supplier: * Print some paste on a board * Reflow the paste * Inspect the quality of the solder connection * Make a decision on accpting the board based on that observation. 2 Have yo
Electronics Forum | Thu Dec 17 17:34:26 EST 1998 | Earl Moon
| Has any anyone established / published quality standards for BGA solder joints? Is IPC-A-610 in process of adding standards for BGAs? | The debate continues. I have felt for some time a maximum 20% voiding is allowable under certain conditions (w
Electronics Forum | Mon Feb 02 12:36:41 EST 2004 | paul_bmc
90% of the assemblies our company produces are class 3 and we have no problem at all inspecting or getting class 3 quality through reflow. Rarely do we have touch up because of insufficient or poorly reflowed solder joints. What are the problems you
Electronics Forum | Tue Feb 03 12:39:20 EST 2004 | paul_bmc
We had the data at the time and it was quite high. More false calls then anything. I do not have the data anymore it since has been archived. When the system was introduced we had 1 engineer and 2 operators trained for programming and running the
Electronics Forum | Tue Feb 03 06:52:45 EST 2004 | paul_bmc
About 2 years ago our company tried to go with a post reflow AOI inspection. This AOI was suppose to be able to inspect to a level class 3 product. **It is impossible** You cannot inspect for a heel fillet and inspecting for poor wetting is a very
Electronics Forum | Mon Feb 06 17:19:59 EST 2017 | davef
Evtimov: IDEALS Project was one of the first to talk about componebt and board damage caused by LF soldering temperatures. There's lots of more current stuff on the web. Here's some that may help: * Assessment of Long-term Reliability in Lead-free As
Electronics Forum | Tue Feb 19 11:27:25 EST 2019 | emeto
Thanks Rob, actually the thermal relieve is very poor. We did attach the thermo couples on the pad so that is checked. I will now check solderability.
Electronics Forum | Tue Feb 19 10:47:47 EST 2019 | rgduval
I'm with Steve. Check the datasheet, and make sure that the terminations are meant for solder application, and not conductive epoxy. I had that happen a year or so ago with an MLCC. Drove us nuts for two days (not to mention the significant rework