Electronics Forum | Mon Jul 31 20:34:58 EDT 2017 | zsoden
Hi all, it has been a bit of a delay but I've finally had a chance to do some further investigation on this. First off, we spend some time to clean the solder bath using Kester Solder Saver and scooped out a lot of crap. We then added about 5kg of
Electronics Forum | Wed Feb 14 16:58:12 EST 2018 | cbart
you would be best to get this from your paste/solder manufacture. but here are some rules of thumb: -Solder paste out of fridge before use - get out the night before needed.. don't let your op's warm on the oven!! you will regret that! if not over ni
Electronics Forum | Sat Feb 22 11:37:00 EST 2020 | kylehunter
Hey all, I've made a post in the past about us expanding to a new space, but I wanted to do a new post with specific questions. We currently have a DEK 265, Phillips Opal Xii, and a Heller 1500. Our main reason for expanding is to have a lead-free
Electronics Forum | Fri May 14 16:08:38 EDT 1999 | Chrys Shea
| | | | | I am looking for anyone who has converted over to VOC Free flux. I need some info on any problems, etc. that you might have had. | | | | | | | | | | Please E-mail me at wes.ruggles@vickers-systems.com or call at (513) 494-5229 | | | | | |
Electronics Forum | Sat Jan 16 02:43:21 EST 1999 | Earl Moon
| Hello, | | We are qualifying new sources of PWB vendors. We've got the first lot of "produciton" boards in and we want to put them through the paces before turing the vendors on. | | So far, the tests I can think of performing, and that we have
Electronics Forum | Thu Jun 17 22:10:48 EDT 1999 | Earl Moon
| | | Does anyone know where I can find a list of things to do to when troubleshooting issues during the wave solder process? | | | | | | for example: | | | | | | Solder Bridge | | | 1.verify amount of flux been aplied. | | | 2.verify turbulance on
Electronics Forum | Wed May 09 10:40:10 EDT 2001 | davef
First, your primary side component pads should be designed according to SM-782A, "Surface Mount design & Land Pattern Standard". Next if you did that and your secondary side component pads are the same size as your primary side components, your diff
Electronics Forum | Fri Sep 24 10:57:18 EDT 1999 | Earl Moon
| Hi Folks: | | We've been having bridging problems on our fine-pitch QFP's, despite thorough inspection of paste height, volume, and placement accuracies....profiles look good also. | | The bridging is happening after coming out of reflow...one la
Electronics Forum | Wed Apr 28 12:48:02 EDT 1999 | Justin Medernach
| | | We use Immersion Gold (AuNi) for our 20 mil pitch and BGA boards. | | | Lately, we have been having solderability problems with boards with this surface from some of our suppliers. | | | | | | We are considering trying boards with White Tin so
Electronics Forum | Mon Mar 15 09:38:30 EST 1999 | Chrys
| Does anyone have any recommendations on spray fluxers? Are there major differences between the high priced ultrasonic machines to the low priced flux/air spraying machines? We are going to be spraying an OA flux with 11% solids content. Are there a