Electronics Forum | Sat Apr 14 00:04:21 EDT 2001 | zam_bri
I'm not a Wave soldering guy and my friend have asked me a question on what is the best preheat time and temperature for Wave soldering.They experiences only 10% flow up thru the PTH barrel. I've asked them to increase the temperatue to 120 Deg C. Cu
Electronics Forum | Mon Apr 16 12:59:51 EDT 2001 | Mike R
If you will place a temperature strip on the board during wave soldering process you will get a max of 210 F or 98.8 C which is normal on the standard wave temperature. The problem on the 10% solder on the TH via hole can be caused by insufficient fl
Electronics Forum | Sat Apr 14 03:25:04 EDT 2001 | kpliew
Hi , As far as I experienced with wave reflow. If u have a refective thermal reader , u will see that the board is exposed to much more temp than the 120 deg that u set. Actually , once u see the board warp or comp. crack u should know that
Electronics Forum | Sat Apr 14 03:25:10 EDT 2001 | kpliew
Hi , As far as I experienced with wave reflow. If u have a refective thermal reader , u will see that the board is exposed to much more temp than the 120 deg that u set. Actually , once u see the board warp or comp. crack u should know that
Electronics Forum | Fri Nov 05 21:41:46 EST 1999 | chartrain
Temperature vs time is what soldering is all about. The faster you run your conveyor, the more heat will have to come from the pot for a given assembly. Example: You heat the board to 200F top side through the preheaters. Eutectic 63/37 melts at 361.
Electronics Forum | Wed Jun 12 04:02:00 EDT 2019 | liyunqiong
SMT reflow soldering temperature setting and process flow: The influence of SMT reflow process parameters on the key parameters of reflow soldering temperature curve provides reference for the setting and adjustment of reflow soldering process para
Electronics Forum | Fri Oct 08 10:08:48 EDT 1999 | Glenn Robertson
| | | | I have a board, 4 spacers needed to be soldered on the board | | | | first with the normal 62Sn37Pb alloy. Then, capacitors are manually soldered on the boards. The density of the board is quite high. If we wave soldered capacitors first,
Electronics Forum | Tue Dec 16 15:43:50 EST 2003 | patrickbruneel
Kev, I looked up records of various hollis machines with 3 preheat zones. and with progressive preheat temp. of 300 400 and 500 with a speed of 3.5ft/min the topside board temp was 120C before entering the wave. the preheat elements were infrared. W
Electronics Forum | Wed Dec 17 08:49:04 EST 2003 | patrickbruneel
Kev, It looks like you have a preheating powerplant and you still only get the board up to 85 Deg. This indicates that the preheating is out of calibration or the range settings might be very wide (Fex the preheat elements shut down at 500 and go ba
Electronics Forum | Tue Dec 16 06:42:51 EST 2003 | Kev
I am having problems achieving correct pre-heater temperatures with our Hollis solder wave. Our original "Verification Golden board" program uses a conveyor speed of 5ft per minute and pre-heat temps of 300, 350, 400 respectively. Our "golden Board"