Electronics Forum | Wed Mar 28 14:11:19 EDT 2007 | pjc
It should only be a visual thing. What may be happening is that all the thermal energy being driven into the wave solder pallet to get good soldering is causing the no-clean residues to burn up a bit, causing the discoloring. Check to see if they hav
Electronics Forum | Fri Jun 12 23:52:42 EDT 2015 | armandogomez
Reflow? or Wave solder? or selective wave solder? For what I understand you problems is with the preheaters you have a high temp that dries up the flux, and when hits the wave is doing that, do you have a thermal profiler? what's the temp just befor
Electronics Forum | Mon Jun 12 10:57:51 EDT 2000 | Jason
I am new to wave soldering. Any information is greatly welcomed. Here is the problem. After soldering the boards they have a film on the bottom of them and sometimes a white powder looking substance. I have tried decreasing the amount of flux on
Electronics Forum | Fri Jun 12 11:15:50 EDT 1998 | Ryan Jennens
Hey all! The wave solder warrior is back. I have found a flux which leave almost no residue (the least yet), but because of its super low solids content I absolutely cannot get topside fillets. The multi-layer, two sided board is on a pallet w
Electronics Forum | Mon Dec 30 23:37:47 EST 2019 | agoesfirmanto
Hello All, I am a SMT Engineer from Indonesia, I am facing the problem of soldering balls in only one IC location, in other areas there are none. solder ball defect almost 30%. I have done several actions but failed to reduce the solder ball. 1.
Electronics Forum | Thu Nov 17 20:51:16 EST 2005 | cangly
Morning Mike, We use Pb63/Sn37, Alpha Metal alloy. Solder pot is at 250 C. The profile of board after Preheat about 100 C, Lambda Wave about 220C (use both Lambda and Chip wave), DWell time 2.1s ~ 3s. Conveyor speed 1.5 in/min. We run by bare board a
Electronics Forum | Thu Nov 17 13:13:49 EST 2005 | Mike
Hello, Some questions.... Are you running lead free? What alloy? What�s your pot temp at? Temp of the board after preheat? Are you getting any solder in the barrels (
Electronics Forum | Fri Apr 22 11:21:42 EDT 2005 | HUH
There are several types of lasers to do laser soldering. Panasonic also has a high intensity light that can solder as well. I've tried em' all and two over whelming things stand out when it comes to this type of soldering. #1 is preheat. It seems
Electronics Forum | Sat Jun 24 07:23:06 EDT 2017 | tch
You will need to preheat the boards for a lead free selective solder process. A preheat module is critical for any wave or selective solder process, if you don't get the board preheated properly the solder is going to resist flowing to the top of the
Electronics Forum | Tue May 17 10:11:54 EDT 2005 | russ
I would use a foam fluxer since spraying rosin will make the stickiest nastiest mess you can imagine. 18 layer board huh? You will want convection preheat, both top and bottom preheaters, preheat tunnel of at least 4-5', a chip wave, laminar flow w