Electronics Forum | Wed Feb 28 19:44:50 EST 2001 | pzohbon
I am having problems with voids in our soldering process. I believe it to be the fact that we use a no clean flux without control on how the boards are handled (gloves, procedures, etc.) Does anyone have suggestions on the appropriate place to start?
Electronics Forum | Tue Mar 06 03:29:05 EST 2001 | daled
Hello I am looking for any data that confirms the long term reliabilty of no clean paste as opposed to water soluable. Does anyone have any past experiences of problems when changing over from water soluable to no clean in the SMT prcocess?? Thanks i
Electronics Forum | Tue Mar 06 14:10:52 EST 2001 | CAL
Are the voids in the balls of a BGA? Are you verifying this through x-ray if they are? some voids depending on size and location are some what accepted. Solder paste type? Solder paste date code? Humidity high? PCB's been stored in a truck trailer?
Electronics Forum | Fri Mar 02 08:52:20 EST 2001 | markkrmp
Are your voids looking like blow holes also? Is this only occurring on the solder joints of the Thru Hole components and Via's? Or does this happen on SMD pads? My experience is that we have seen this but only with some of our older PCB's which are
Electronics Forum | Wed Mar 24 11:09:44 EDT 2010 | rajeshwara
Hello Sir I faced the same problem for QFP in DTH product in India. IPC stated that void should not be more than 25% of solder joint. But this type of void definatly create problem during functional test. Please check the folloeing point... 1.Check t
Electronics Forum | Wed Mar 24 10:28:51 EDT 2010 | Sean
Hi all, Anyone used to come across solder void underneath mosfet as shown in the attached file? Will this pose any reliability issue, such as get burnt during functional test? How to over come this problem? As far as I know there is no acceptabl
Electronics Forum | Thu Mar 25 12:34:26 EDT 2010 | bgaguy
the voids will cause a long term relability problem as the part will not be correctly heatsinked. Change your stencil aperature to a "+" sign 15-20 mils wide in the center of the pad. ___________ : | : : | : :----|----: : | : :__
Electronics Forum | Fri Mar 26 00:57:05 EDT 2010 | 89jeong
Hello Sir. We also have faced a same problem. At that time, we had to repair it because we could not find any solution. But in our experience, the void underneath FET was more severe whenever we used the FET that have been made long time ago. It is
Electronics Forum | Fri Mar 26 03:24:01 EDT 2010 | ravikumarasahitec
Hi, yes we used to see this kind of problem our customer end. This due to stencil aperture opening.these kind of issues we will overcome thorough our stencil process. please contact. ravikumar@asahitec.in
Electronics Forum | Wed Feb 20 09:29:19 EST 2008 | mun4o
ni, I had similar problem too.I bake PCB in SW mashine - about 8h ,T=90 C.Problem is in the base material of PCB - there are moisture in the material.After my complaint to PCB factory , they change material and the problem disappear.