Electronics Forum | Wed Aug 10 12:05:11 EDT 2005 | Rob
Hi Pr, No idea what the material is - we haven't usd it for a while now, but it was flush & didn't cause any printing problems on double sided reflow. Your board house should know all about it - I would suggest some but ours are all UK or China/Tai
Electronics Forum | Tue Aug 10 07:28:49 EDT 1999 | Brian
| | | I am having cleaning problems when processing PCB's which have | | | TAIYO solder mask on them. After processing, hand soldering and | | | cleaning, a sticky residue is remains, resulting in a cosmetically poor finish with tide marks etc. Other
Electronics Forum | Tue Aug 10 15:19:55 EDT 1999 | Earl Moon
| | | | I am having cleaning problems when processing PCB's which have | | | | TAIYO solder mask on them. After processing, hand soldering and | | | | cleaning, a sticky residue is remains, resulting in a cosmetically poor finish with tide marks etc.
Electronics Forum | Tue Aug 10 15:47:34 EDT 1999 | John Thorup
| | | | | I am having cleaning problems when processing PCB's which have | | | | | TAIYO solder mask on them. After processing, hand soldering and | | | | | cleaning, a sticky residue is remains, resulting in a cosmetically poor finish with tide mark
Electronics Forum | Tue Aug 10 16:01:12 EDT 1999 | Earl Moon
| | | | | | I am having cleaning problems when processing PCB's which have | | | | | | TAIYO solder mask on them. After processing, hand soldering and | | | | | | cleaning, a sticky residue is remains, resulting in a cosmetically poor finish with tid
Electronics Forum | Mon Aug 09 18:03:28 EDT 1999 | Earl Moon
| | I am having cleaning problems when processing PCB's which have | | TAIYO solder mask on them. After processing, hand soldering and | | cleaning, a sticky residue is remains, resulting in a cosmetically poor finish with tide marks etc. Other solde
Electronics Forum | Mon Aug 21 19:38:33 EDT 2000 | Dave F
Eric: I�ll pass on the uV and ammonia, also. Thoughts are: 1 You�re correct that the temperature/humidity mix can be a big driver to latex peelable solder mask cure time, but don�t overlook material thickness. Dispensers put material in a very th
Electronics Forum | Tue Sep 21 16:09:08 EDT 2004 | davef
Q1: What is "enough surface free energy"? A1: Look here for background: http://www.azom.com/details.asp?ArticleID=1575 Q2: How do I determine surface free energy? A2: We look at it a relative term. For instance, a semi matte finish on solder mask
Electronics Forum | Sat Nov 08 09:42:22 EST 2003 | ethercom
Hi: I have seen this problem before. It is caused by improper curing of solder mask by the fab manufacturer. When you run the board thru' wave solder, and then wash the board, you see the problem of white residue. However, when you apply heat, you c
Electronics Forum | Fri Nov 07 12:48:31 EST 2003 | rholland
I have seen in the last couple of months more boards with a white hazing under the solder mask. I ran a few tests on a board to determine the cause of the white hazing underneath the solder mask. First I confirmed, or at least I think I confirmed, t