Electronics Forum | Sun Aug 02 19:47:16 EDT 2009 | isd_jwendell
Now that I've seen the pics... Soldering could work just fine. If you are going for large production then you could get copper discs cut and mounted in tape carrier ($$). This would make it very easy for automated equipment to assemble. Mounting a
Electronics Forum | Fri Aug 07 07:55:30 EDT 2009 | robhs
Hi. We are planning a production run of a board that utilises the SEMTECH SLP2710P8 8-pin device (2.7 x 1.0 x 0.58mm). The part orientation on the board necessitates that the squeegee print direction approaches the stencil apertures on the long side
Electronics Forum | Fri Aug 21 13:45:12 EDT 2009 | rossi
We are using a vapor phase oven which we have used successfully for a number of years with both leaded and unleaded solders. Recently we experienced problems with a no lead BGA that has low silver balls. The problem is that the soldered boards do no
Electronics Forum | Wed Nov 30 15:47:50 EST 2011 | upguy
We have used the Excel macro with great success for our two MyData TP9-UFP machines running TPSys version 1.5.18. It will run in Excel 2000, Excel 2002 and Excel 2003. It will not run under Excel 2007 and later or under StarOffice. I can send the
Electronics Forum | Tue Aug 25 03:24:11 EDT 2009 | fiona_j
Hello, I have been recently bringing a new RoHS wave soldering machine into production. Unfortunately, I am finding many of the boards are experiencing blow holes. It is always silver plated PCBs and I believe it is related to moisture ingress. I n
Electronics Forum | Wed Sep 23 03:43:31 EDT 2009 | d0min0
hello, we are profiling with the pcb each day - results are very good with a small delta we made another test board with TC only in the problem places - same good result we tried 500-600 boards on 12 zone machine - zero defects while on standard 6
Electronics Forum | Wed Sep 02 02:45:01 EDT 2009 | rocko
Hi All, Let me summarize the key facts and findings: 1) This is not a permanent problem. Only one production batch was affected. The cleaning solution was exchanged and now the cleaning process runs normally. 2) Probably the residues are not ion
Electronics Forum | Wed Oct 14 09:01:16 EDT 2009 | jasonduerr
Hi, Everyone! What do you use for Assembly Drawings? I need Electronics Assembly Drafting software, and I am hoping to hear your recommendations. The core functionality I need is the ability to translate X/Y coordinates (ASCII file) to my Gerbers
Electronics Forum | Sun Nov 01 23:51:44 EST 2009 | boardhouse
Hi Julie, My opinion is that the top board would not pass IPC, solder mask encroachment on pads. Second board is what we call Orange peel,this can be caused two way's. 1) the solder mask was not tack dried enough prior to imaging which caused artwo
Electronics Forum | Thu Oct 29 07:56:45 EDT 2009 | jeffreyj
Thanks for the reply, Sr.Tech. Sure, I'm considering all of the things you've mentioned. It certainly seems that service and spare parts are easy to obtain for the Quads, which is the main reason I am even considering the dinosaurs (that and they ca