Electronics Forum | Sat Apr 27 21:56:50 EDT 2002 | yngwie
Thanx for the feedback. The solder mask is PSR-4000 ( need to confirm this - not too sure ). If the board got in touch with the solder bath, for the contact time of 3 - 6 secs, this should not be the case for proper curing process right ?. thanx ag
Electronics Forum | Mon Apr 04 22:40:07 EDT 2005 | davef
We'd contact suppliers of LPISM. Top LPISM available in the United States are: * Coates ImageCure XV501T & XV501TSM * Coates ImageFlex (Flexible Solder Mask) SV 601T * Enthone DSR 3241 and DSR 3241 GM * Rogers RFlex 8080 LP1 & RFlex 8080 LP3 (Flexib
Electronics Forum | Sun Aug 16 16:01:06 EDT 2009 | davef
White, lead free * Taiyo America PSR-4000 LEW1 * Huntsman (formerly Vantico, formerly Ciba Geigy) Probimer 77 white solder mask Also, search around LEDs Magazine [ http://www.ledsmagazine.com/ ]. White solder masks are often used as a reflective ba
Electronics Forum | Fri Apr 16 12:47:48 EDT 2010 | boardhouse
White solder mask does have a tendency to yellow within the lead free environment. so double coating will not help any. I due believe the flux is a factor in the yellowing but due to the color is the main reason. Find out what brand of S/M mask they
Electronics Forum | Thu Jun 13 21:44:21 EDT 2002 | jkhiew
Hi all, * Defect : termial to terminal touching btw two melfs body that created short circuit. * Clearance : 0.8mm btw two melfs body. * Size melf : diameter=2.4mm to 2.7mm, length=4.8mm to 5.2mm * Stencil opening : "v" shaped to minimise component
Electronics Forum | Thu Mar 12 03:14:14 EDT 2009 | nibirta
Thank you for support. As i promised you, I am coming back with the results. The SM used was Probimer 77 with Kester 979 flux. The supplier says that there is an incompatibility and we have changed the flux with IF2009M. Same problem! They have chan
Electronics Forum | Mon Jul 01 20:45:38 EDT 2002 | davef
Solder mask thickness specifications by fabricators are: * Wet mask: 0.0002 ~ 0.0004� on trace * LPI mask: 0.0002 ~ 0.0008� on trace Liquids usually range between 10 to 13 um (0.00039 to 0.00051") when dried. Liquid resist processes I have seen are