Electronics Forum | Wed Aug 25 21:25:28 EDT 2004 | davef
First as a nit, your �substrate� is probably NOT copper. It�s probably FR4 fiberglass/epoxy. Substrate. Base Material. A supporting insulating material upon which parts, components, and elements are attached. Second, enough of that, on to your i
Electronics Forum | Tue Aug 02 15:03:37 EDT 2016 | davef
On a previous black pad experience we soldered a wire to a fiducial and did a pull test to failure. On the black pad board the wire and solder pulled of clean leaving the fiducial on the board. On good boards the copper came off with the wire. If you
Electronics Forum | Mon Oct 25 17:50:46 EDT 2004 | Mike
I work for a PCB Manufacture and I am looking for info on BGA Pull test or strenght test. I have a CM that is experiencing bga's with some weak joints. they are telling me that when they do their pull test the joints are breaking at the nickel inste
Electronics Forum | Mon Oct 25 21:49:14 EDT 2004 | davef
First, any results of pull or shear tests are unscientific at best. [We pop our BGA from boards with, appropriately enough, a beverage can opener.] Second, we have no have problems with your ENIG specification. Third, as with your customer, we'd e
Electronics Forum | Thu Aug 21 17:17:47 EDT 2003 | justin
Do some push / pull testing. Typically with black pad, you can flick the components right off the board. If you have this, the boards are about as reliable as a Yugo. If you get decent push / pull results, odds are you don't have black pad and you
Electronics Forum | Tue Oct 26 08:41:56 EDT 2004 | Bob R.
When we first got into BGAs on ENIG we were getting joint cracking at in-circuit test. The joints were breaking in the Sn-Ni intermetallic. We did a lot of pull testing while working with our board suppliers and our conclusion was that pull testing
Electronics Forum | Thu Oct 24 14:10:53 EDT 2002 | Terry Burnette
I've been informed that I can't post the Dye Penetrant paper on the SMTNET library till Advanced Packaging releases the paper in their Dec. issue. You should be able to pull a copy in the next couple of weeks from their site, http://ap.pennnet.com/ho
Electronics Forum | Wed Aug 24 22:11:36 EDT 2016 | davef
I'd guess that "black pad" is not the issue that you need to address, because only 2 of your 5 test points has the problem that we seem to be discussing. I'd expect "black pad" problems to be more wide spread. Something is going on at those two locat
Electronics Forum | Tue Feb 11 15:54:23 EST 2003 | Jodi Roepsch
I am interested in knowing if anyone has new information about the black pad defect with ENIG plating. I am interested in it from the viewpoint of risk assessment, testing done on final product to isolate failures,and root cause of the defect. Than
Electronics Forum | Mon Mar 17 15:32:33 EST 2003 | Jodi Roepsch
Thanks to everyone who took my question seriously and made an effort to share information on this topic. I have done extensive literature searches on this topic in the past but am still looking for more information regarding how this defect affects