Electronics Forum | Sun Jul 29 21:23:27 EDT 2001 | nifhail
When carry out the contamination test,do we measure for Chlorides on water soluble and No-clean fluxes? 1) What is the equivalent factor for machines developed to test the board cleanliness, Omega-meter vs Ionograph vs Zero-ion. 2) What values do we
Electronics Forum | Mon Sep 11 04:23:49 EDT 2000 | Wolfgang Busko
Adam: I would say that you do have a reliability problem. - check parts for solderability - check your board finish - check your profiles - check your paste - check your processes with focus on cleanliness - do some mechanical tests, you should rath
Electronics Forum | Mon Sep 11 04:10:46 EDT 2000 | Jim Arnold
I spent 25 years operating my own hybrid shop working with surface mount components, soldering materials and procedures. Dealing all the while with it's associated surprises and problems such as yours. Now-a-days I get paid to investigate and attemp
Electronics Forum | Wed Dec 22 05:42:19 EST 1999 | Wolfgang Busko
Hi John, I�ve seen problems some sites have or had with bridging problems in the wavesolder process with 1206 and 0805. Adjusting the system and focussing on the flux parameters sometimes improved things. With some older systems it was hard to get s
Electronics Forum | Mon Nov 01 16:41:58 EST 1999 | Robert Culpepper
Hello Mark, I can�t provide any hands on feedback with 0402 packages but we are using a no clean process with 0603 devices. Here are some parameters which will affect solder balling. Stencil thickness, aperture size, paste viscosity, snap off and bot
Electronics Forum | Mon Oct 04 07:48:34 EDT 2010 | scottp
When you break them where is the failure? Is it the solder joint (doubtful), the part termination, the body of the part, or the board? If in the solder joint, is it in the bulk solder or intermetallic? If in the part, what direction is the crack?
Electronics Forum | Wed Sep 29 09:35:39 EDT 2010 | blnorman
Can any body help me that how can I check the > strength of the 0603 capacitor & how much it > should be? Is there any standard for the > soldering strength of the Diffrent SMT > packages. Manjeet singh I'm not aware of a standard that provides
Electronics Forum | Mon Oct 04 00:26:07 EDT 2010 | mskler
I want to check this becuase we are exporting the PCB & there is problem of components missing at customer end in some PCB while we are doing 100% AOI & then ICT testing. These components are checked by both. there is no possiblities that the compone
Electronics Forum | Thu Apr 28 20:30:20 EDT 2005 | russ
Are we talking pushing on leads to see if they come loose?
Electronics Forum | Fri Apr 29 11:21:35 EDT 2005 | jsloot
I have heard the term as both green stick and orange stick, but yes, pushing on the leads to detect un soldered leads. The amount of force is subjective. Any thoughts on this is appreciated.