Electronics Forum | Wed Apr 21 21:50:28 EDT 2004 | adam
Hi I recently having problems on the components having non wetting on the flex circuits. The profile that I am using is according to the solder paste suppiler recommended. Can anyone pls. advise? Regards
Electronics Forum | Wed Sep 15 20:59:23 EDT 2010 | genesan
hi All, Here i snap shot previous PCB(HASL) and current PCB(Immersion Silver).Base on the photo it could be PCB oxidize cause the non wetting?
Electronics Forum | Tue Sep 14 00:22:08 EDT 2010 | sachu_70
Hi Gani, non-wettting issues can surely be resolved. At first, would appreciate if the following info could be shared. Do you supply just one PCBA product to this client or is the complaint towards one of the many products that you deliver? Also, doe
Electronics Forum | Mon Apr 26 17:12:14 EDT 2004 | babe
Take a solder iron with some wire solder and attempt to tin the leads of the component. Look under magnifier or microscope. Did they wet? If not try fluxing them with liquid flux and then soldering again. Did they wet? If they did not then you may wa
Electronics Forum | Tue Sep 14 13:37:51 EDT 2010 | dan_ems
Hi Gany, did you check the temperature at reflow profile on this BGA ?
Electronics Forum | Wed Sep 15 01:16:36 EDT 2010 | dan_ems
Hello, what type of solder paste use, and this component is made for lead process?
Electronics Forum | Wed Sep 15 03:04:13 EDT 2010 | genesan
kester 562 clean process and this leaded part.
Electronics Forum | Thu Apr 22 04:55:42 EDT 2004 | Richard
Have you tried using Concoat MUST II solderability tester to test on the component terminal are of good solderability. Non-wetting may occur due to oxidation or contamination on component terminal. So for immediate response to you problems is to used
Electronics Forum | Tue Sep 14 04:00:12 EDT 2010 | genesan
Hi Sir grahamcooper22, There should not a issue in stencil since i had open the aperature 1:1(one to one).Futhemore this is HASL pcb coating as now our customer had convert to immersion silver.I had do comparison between both and found HASL wetting n
Electronics Forum | Thu Apr 22 21:34:58 EDT 2004 | adam
Thanks guys. I am from a subcon, we can't change the solder paste supplier and there is only one approved vendor for this component. I think I will try on the component solderability. Regards