Electronics Forum | Tue Jul 27 11:32:20 EDT 2004 | dwanzek
Thanks for the input guys. One problem with this theory, we see the same failure using Omni 5000 solder paste. We also see this problem across 4 production lines, suggesting it is not oven related. The profile meets recomendations and we have tried
Electronics Forum | Thu Jul 15 22:03:07 EDT 2004 | KEN
In no particular order: Will the failed joints wet when touched with an iron + flux? Is there flux surrounding the joint (post reflow). If no, you may be baking it out premateurely. Is this assembly wave soldered? Where is defect discovered in yo
Electronics Forum | Thu Aug 05 05:23:13 EDT 2004 | Bryan
Hi All,per my understanding ,the fail mode is the heel fillet of QFP seems no good,right?If yes...I think..we should:1.increase the aperture length on stencil and make sure there's enough solder paste on pad before reflow. or you can increase your t
Electronics Forum | Thu Jul 15 18:07:04 EDT 2004 | dwanzek
This has been a tough one to date. Any ideas will help. Problem definition � random QFP144 part not soldering all leads. Percentage fallout is about 1-5% of boards. Usually leads, one or more, on trailing side to the direction of travel does not wet
Electronics Forum | Mon Jul 19 21:25:28 EDT 2004 | davef
It seems like the flux is burning-up before the metal begins to flow on this slightly odd component. Alpha talks about alternate reflow recipes for WS609, as follows: * A straight ramp up profile is preferred for reflowing low to medium thermal mass
Electronics Forum | Tue Aug 18 02:10:14 EDT 2009 | sergey2007
Hello, I have a customer who recentely installed a vapor phase soldering system. Everything goes pretty well, but from time to time the customer has the same problem with the soldering: one of the components on PCB (usually, it's a QFP package) is ro
Electronics Forum | Fri Jun 09 12:13:11 EDT 2006 | Chunks
Rob and Pete are both right. "We" had the same problem, with just one manufacturer of the same style QFP (don't want to name names here). We had the same style of QFP from a different manufacture right next to the problematic one on about 3 product
Electronics Forum | Thu Jun 08 23:26:28 EDT 2006 | Shawn Vike
We are a small company, reletivly new to doing our own SMT (1 year) and we are having an issue, I think. We manufacture many board with no problems, but we have one that constently defeats us. This particular PCB has ENIG finish, and we have had th
Electronics Forum | Fri Sep 14 02:18:32 EDT 2001 | gsparka
Hi. After reflow soldering. There are lots of non wetting of leads. 71 b'd all are mounted resister,condensor,qfp,plcc,bga have got the defects so many. all defecs occured in the fine pitch ic. others are good. On some fine pitch pads not mou
Electronics Forum | Mon Aug 22 13:28:47 EDT 2011 | scottp
No, don't put weight on it. If the part is really "floating" on the solder and not wetting properly and the solderability looks good on all your other parts then I'd suspect a part problem. Get with the QFP supplier and make sure the Sn isn't too t