Electronics Forum | Fri Aug 06 03:51:06 EDT 1999 | Thomas
Could someone give recommendation on the stencil opening for printing epoxy on HAL FR4 PCB for 0805 and 0603 size chips capacitors and resisitors. My regular stencil manufacturer recommend the following: Thickness: 8 mils 0805 opening: Oblong 0.35 X
Electronics Forum | Sat Aug 07 11:10:03 EDT 1999 | JohnW
| Could someone give recommendation on the stencil opening for printing epoxy on HAL FR4 PCB for 0805 and 0603 size chips capacitors and resisitors. | My regular stencil manufacturer recommend the following: | Thickness: 8 mils | 0805 opening: Oblong
Electronics Forum | Sun May 21 09:38:25 EDT 2006 | davef
Epoxy Removal and IC Delidding [Hardware Hacking: Have Fun While Voiding Your Warranty, Chapter 14] Encapsulation of critical components using epoxy or other adhesives is commonly done to prevent tampering and device access (the microprocessor shown
Electronics Forum | Tue Aug 03 08:38:42 EDT 2004 | davef
Conductive epoxy is usually specified as less than 6:1 aspect ratio fill capable, while non-conductives are 10 to 14:1 (depends on which brand and who you ask).
Electronics Forum | Tue Aug 03 14:46:25 EDT 2004 | russ
We recommend to the designers "the smallest diameter that you can get away with", that will help reduce the solder scavenging into via diring reflow. unless you are planning on having them filled as Dave F mentioned. Russ
Electronics Forum | Thu Jan 05 16:35:16 EST 2006 | Amol Kane
correct, I am in the process of recommending the correct material, process and logistical variables to the customer to help them transition to a LF product
Electronics Forum | Wed Jan 04 10:34:04 EST 2006 | DannyJ
I don't believe you are missing anything, Amol. Mainly, you just need to make sure that your oven handles the higher temperatures needed for reflow. Also, there has been a lot of discussion on how many zones are needed to properly reflow lead-free
Electronics Forum | Thu Aug 05 12:51:19 EDT 2010 | peteb
Need recommendations on brands and models of reflow ovens for lead free. Small benchtop for prototyping and short runs. Board size about 10" by 10". What works well? What to stay away from? Thanks for any input and advice.
Electronics Forum | Thu Sep 02 21:02:55 EDT 1999 | Paul Wareham
We've noticed that there are many different recommendations for pad sizes for various SMT parts. This seems to vary wildly from manufacturer to manufacturer for the same case sizes. Is there any standards that can used used to specify these sizes?
Electronics Forum | Thu Oct 17 00:34:59 EDT 2019 | jani
Hi, We have solder reflow use with water soluble flux and Tin/lead process. There is special glass component which needs to mask during reflow soldering and wash flux+solder mask post soldering. The existing solder mask does washes off. But leaves