Electronics Forum | Fri Aug 20 14:22:02 EDT 1999 | Earl Moon
| | | I am being asked, by my vendor and Purchasing people about converting from Tin/lead pads on P.C.B's to Electroless Tin Plating. | | | Can any one tell me what I have to change in my SMT | | | process (paste, reflow, etc) If any? | | | I
Electronics Forum | Tue Aug 10 07:47:12 EDT 1999 | Brian
| | | hello to everybody, | | | we have a really satisfactory no clean process, both smt/reflow and wave soldering, but we get troubles with defects rework; | | | does anybody know how to eliminate flux residues or how not to produce them during rew
Electronics Forum | Tue Aug 10 20:22:15 EDT 1999 | Wayne Sanita
Hello, Could be that touchup operators are using too much flux. What are you dispensing flux with. Disposable or refillable flux pens are good to have around. | | | | hello to everybody, | | | | we have a really satisfactory no clean proc
Electronics Forum | Wed Aug 04 16:43:58 EDT 1999 | John Thorup
| We are installing a new reflow oven and I have been told that we do not need to vent the exhaust out through the roof since we have a false ceiling. All that is required is to vent above the false ceiling and that the air exchange is great enough t
Electronics Forum | Thu Aug 05 10:46:20 EDT 1999 | Dave F
| We are installing a new reflow oven and I have been told that we do not need to vent the exhaust out through the roof since we have a false ceiling. All that is required is to vent above the false ceiling and that the air exchange is great enough t
Electronics Forum | Fri Jul 30 17:22:48 EDT 1999 | Dave F
| | Surface Mount Components like QFP's in Tray usually comes sealed in an anti-static plastic pack. In case the QFP's were removed from the said anti-static bag for more than 2 weeks, do these components needed to be baked for they might produce so
Electronics Forum | Fri Jul 23 12:49:47 EDT 1999 | Tony
| There is a practise within the industry of an Inspector inspecting a board, and that same Inspector performing touch-up. My opinion is that the Inspection and Touch-up operations should be separate functions whereby the Inspector is not performing
Electronics Forum | Fri Jul 23 09:01:36 EDT 1999 | Earl Moon
| HI Earl | Thank you for your answer. | Let me know you about the hot you mentioned | First of all, The rework machine is the BGA3500 (manufactured by 0.k international:U.S.A) | ��DESOLDERING HEAT :OVER 200��(CENTIGRADE),30SEC(CHECKED
Electronics Forum | Thu Jul 22 22:57:14 EDT 1999 | Earl Moon
| Does anyone have any experiences with bga reballing. | When I had reworked failed bga part with new part It was good. | So I tried to reball bga detached but failed . | I guess the cause of fail is thermal shock. | IS IT OK TO REBALL BGA PARTS
Electronics Forum | Wed Jul 21 20:52:52 EDT 1999 | Scott
| | I have pcb's in which i am experiencing warping. | | the boards are 12.8125" on a diagonal measurement. | | they are out approximatley .010". | | the boards are combination thru-hole,smt, they also have 3ounce copper.what is acceptable,and what i