Electronics Forum | Mon Jan 29 06:44:59 EST 2001 | Scott B
I have recently come across a device which has a palladium over nickel finish which when soldered shows evidence of poor wetting to the lead ( i.e. a wetting angle greater than 90�) about three quarters of the way up the side of lead. This is only vi
Electronics Forum | Thu Mar 31 17:27:36 EST 2005 | russ
Are we possibly talking palladium instead of platinum? I haven't yet heard of platinum terminations (seems expensive) If it is palladium over nickel, I can tell you that you need to reach 225-230 Deg. C in reflow and the TAL should be about 90 sec.
Electronics Forum | Tue Nov 29 21:51:37 EST 2005 | wmeyers
I have a pin and sleeve assembly that utilizes a fusible link type of solder, Bi, Cd, Pb and Sn alloy. The pin is gold plated, the sleeve is copper alloy 725. I have had sporadic success with wetting of the sleeve during the reflow process. To improv
Electronics Forum | Wed May 11 13:27:30 EDT 2005 | Sam Ho
i want to know which type of solder paste and reflow profile can support the solder pad with nickel but not covered gold on the pcb.
Electronics Forum | Wed Nov 10 10:41:57 EST 2010 | esoderberg
subject board fabrication calls for .05 -.125um of gold over 2 - 5 um of nickel. When doing double sided reflow using same profile, parts of the gold are tarnishing and causing test pad failures. any ideas as to the cause?
Electronics Forum | Thu May 02 09:33:30 EDT 2013 | 15009
Looking for advice on soldering lead free paste to a board with very heavy gold plating. I have learned from the Customer that this is HARD GOLD and that it is 10-20 Micro Inches Hard Gold over 100 Micro inches of Nickel. When we reflowed the solde
Electronics Forum | Thu Jul 15 18:58:48 EDT 1999 | Earl Moon
| We are currently assemblying several different board type with gold plated lands with varying results. Can any of you that has successful experience in this area give me some pointers. What paste do you use? Do you use the recommended reflow pro
Electronics Forum | Tue Aug 20 14:55:33 EDT 2002 | markhoch
Has anybody expierianced solderability issues on electroless nickel boards that do not have gold immersion? We recently tried to process boards of this type, and I may as well have been trying to reflow on plastic. Any ideas?
Electronics Forum | Fri Feb 28 11:02:06 EST 2020 | slthomas
I'm not 100% sure which type of gold you're asking about, but if you're talking about hard gold plating, I think the most common use is to provide a durable surface for things like membrane switch contacts because it resists abrasion and other mechan
Electronics Forum | Sun Apr 05 00:23:53 EDT 2020 | researchmfg
1. To protect the nickel and copper under gold plating from oxidization before soldering. Gold plating can extend the PCB self-life and improve the solderability for 2nd re-flow. 2. Provide a good bonding strength. For Chip on Board process that Gol