Electronics Forum | Fri Aug 13 07:26:06 EDT 1999 | Brian Conner
| | We are using a mixed technology process with mostly through-hole parts plus some SMT IC's on the component side and some passive SMT parts on the solder side. We do not have a proper wave soldering machine for doing solder side SMT (double wave
Electronics Forum | Fri Aug 13 10:19:35 EDT 1999 | Boca
| | We are using a mixed technology process with mostly through-hole parts plus some SMT IC's on the component side and some passive SMT parts on the solder side. We do not have a proper wave soldering machine for doing solder side SMT (double wave
Electronics Forum | Wed Aug 11 15:48:54 EDT 1999 | JohnW
| We are using a mixed technology process with mostly through-hole parts plus some SMT IC's on the component side and some passive SMT parts on the solder side. We do not have a proper wave soldering machine for doing solder side SMT (double wave or
Electronics Forum | Thu Aug 12 19:30:22 EDT 1999 | Kris Harris
| We are using a mixed technology process with mostly through-hole parts plus some SMT IC's on the component side and some passive SMT parts on the solder side. We do not have a proper wave soldering machine for doing solder side SMT (double wave or
Electronics Forum | Thu Aug 01 13:04:57 EDT 2002 | gdstanton
Its interesting. It appears I'm getting conflicting feeback from Indium. This says its not a problem... http://indium.custhelp.com/cgi-bin/indium.cfg/php/enduser/std_adp.php?p_sid=kTDKGClg&p_lva=&p_faqid=355&p_created=1014734692&p_sp=cF9ncmlkc29
Electronics Forum | Sun May 23 10:14:14 EDT 1999 | M Cox
| Has anyone had any experience or data using vibration during the reflow process. | We introduced a vibration device attached to the fixed rail on a Vitronics reflow oven. The reason was to prevent skewing on large PLCC devices. The process worked v
Electronics Forum | Tue May 25 09:19:00 EDT 1999 | Ricardo Lopes
| | Has anyone had any experience or data using vibration during the reflow process. | | We introduced a vibration device attached to the fixed rail on a Vitronics reflow oven. The reason was to prevent skewing on large PLCC devices. The process work
Electronics Forum | Mon May 15 11:03:13 EDT 2006 | Pitt Bull
Can lead free components/assemblies be contaminated if reflowed in a reflow oven for leaded process?
Electronics Forum | Tue May 16 07:03:54 EDT 2006 | smtspecialist
I have only one reflow oven can I use it for both processes (leaded and lead-free)? If I do use it, one run for leaded and the next run for lead-free will that contaminate my lead-free process?
Electronics Forum | Thu Jan 05 16:35:16 EST 2006 | Amol Kane
correct, I am in the process of recommending the correct material, process and logistical variables to the customer to help them transition to a LF product
.gif)