Electronics Forum | Fri May 21 11:59:24 EDT 1999 | John Eramo
Has anyone had any experience or data using vibration during the reflow process. We introduced a vibration device attached to the fixed rail on a Vitronics reflow oven. The reason was to prevent skewing on large PLCC devices. The process worked very
Electronics Forum | Fri Mar 21 20:21:41 EST 2003 | Grant
Hi, I can verify that, and we have done 2 or more reflows with prototypes, using vapor phase reflow, and because there is no oxygen, the result is good, and you cannot tell the difference between the first reflow, and the 3rd. We are getting a vap
Electronics Forum | Fri Nov 24 07:10:39 EST 2000 | Chris May
Sarry, Word on the street is that your profile will have to be hotter, maybe up to 20C hotter, I have trialled lead free. The sales guy said, "Right, lets reprofile your oven ! I said, "No, lets try it as it is.....! The results were fine, as the
Electronics Forum | Sat Oct 10 04:58:18 EDT 1998 | Tony B
| *Reply to: ericr@nj.tanon.com | | Without going into a lengthy explaination {at this time}, has anyone experimented, tested, evaluate, and/or 'perfected' an SMT double-side reflow process. Presently I'm using a Kester R593 OA (water soluble) Sn63/
Electronics Forum | Thu Oct 08 22:32:53 EDT 1998 | E.
*Reply to: ericr@nj.tanon.com Without going into a lengthy explaination {at this time}, has anyone experimented, tested, evaluate, and/or 'perfected' an SMT double-side reflow process. Presently I'm using a Kester R593 OA (water soluble) Sn63/Pb37 -
Electronics Forum | Mon Aug 31 07:56:39 EDT 2009 | d0min0
Hello, since some days we are facing strange problem with SMT component reflow paste on one side of the component is reflowed correctly while the other side is 10%-70% non-reflowed (same component on 3 positions per module, alwyas the same land pad)
Electronics Forum | Thu Apr 15 17:06:08 EDT 2004 | russ
What are your temps at the locations that you are having trouble with. We cannot tell anything by the zone settings of an oven. We need max temp, how long above liquidous etc.. a lot of times this symptom is due to too long of a soak at too high o
Electronics Forum | Sat Sep 19 09:52:09 EDT 2009 | profilingguru
Before you rule out the profile, did you run an actual profile of the board or run machine characterization? How old are your TCs? Have you run them more than a half dozen times? Is your profiler calibrated. In my experience making a living of pr
Electronics Forum | Tue Dec 28 12:55:16 EST 1999 | Justin Medernach
Greg, The best advice that I can give you is a PBGA will respond just like any other surface mount package. There may be a 5 degree delta between a PBGA 356 and a QFP208 but the two respond very similarly in the convection reflow environment. CBGAs
Electronics Forum | Fri Feb 13 08:54:43 EST 1998 | justin medernach
| Hi , | I have not been able to find any good description on how to perform double sided reflow on PCBs.The best would of course be to avoid reflowing the bottom side again but in real life this is not possible. | So when double sided reflow sol