Electronics Forum | Sat Oct 01 01:04:47 EDT 2005 | ck
I face a problem where the components termination is non lead free but solder alloy is lead free. Thus i am using hybrid reflow profile. The specs for the reflow profile i am using: reflow temp. 120 to 160 deg C; time 90 to 120 sec. As for the pak te
Electronics Forum | Sat Apr 11 14:31:16 EDT 1998 | Gary Simbulan
| | I would like to invite everyone to share/discuss | | information/knowledge/experience they have with | | the req's that are assumed to be valid for the | | temperature/time relation in the process of reflow | | soldering Pin In Paste, Intrusive R
Electronics Forum | Tue Oct 04 03:16:14 EDT 2005 | grantp
Hi, I thought it was extreemly bad to use lead based parts with lead free solder? Regards, Grant
Electronics Forum | Fri Jun 26 14:27:51 EDT 2020 | victorzubashev
Hi Indhu, It could be multiple reasons but probably one root cause. metal nut might require reflow profile change- you need to check it with SMT reflow profiler. the part might be oxidized - you can check solderability or try to solder part using a
Electronics Forum | Fri Apr 10 03:52:13 EDT 1998 | Frank J. de Klein
I would like to invite everyone to share/discuss information/knowledge/experience they have with the req's that are assumed to be valid for the temperature/time relation in the process of reflow soldering Pin In Paste, Intrusive Reflow or whatever yo
Electronics Forum | Sun Apr 12 12:55:11 EDT 1998 | Bob Willis
| I would like to invite everyone to share/discuss | information/knowledge/experience they have with | the req's that are assumed to be valid for the | temperature/time relation in the process of reflow | soldering Pin In Paste, Intrusive Reflow or w
Electronics Forum | Fri Apr 10 10:04:44 EDT 1998 | justin medernach
| I would like to invite everyone to share/discuss | information/knowledge/experience they have with | the req's that are assumed to be valid for the | temperature/time relation in the process of reflow | soldering Pin In Paste, Intrusive Reflow or w
Electronics Forum | Mon Apr 13 12:11:41 EDT 1998 | Justin Medernach
| | | I would like to invite everyone to share/discuss | | information/knowledge/experience they have with | | the req's that are assumed to be valid for the | | temperature/time relation in the process of reflow | | soldering Pin In Paste, Intrusiv
Electronics Forum | Mon Apr 13 07:55:48 EDT 1998 | justin medernach
Dear Justin, I am not asking for experiences with ovens as to whether you think they are capable of THT reflow. I am asking more specifically about actual req's and experiences with THT reflow, regardless of the oven used. Your answer does not hold i