Electronics Forum | Thu Aug 06 19:20:09 EDT 2009 | boloxis
easy, just dip the ICs on a very weak solution of Nitric Acid, by very weak I mean like drops of Fuming Nitric acid in a half full DI water beaker. Place the beaker on a Ultrasonic bath and dip/shake the ICs in the solution in 5~ 10 seconds only. You
Electronics Forum | Tue Sep 11 22:52:18 EDT 2007 | davef
Here are some options for removing OSP coatings from pads of the BGA substrates. * Leave the substrates in storage for 13-14 months. Shelf life of OSP coating is ~12 months, depending on the product. * Wash the substrates in your aqueous washer. Ea
Electronics Forum | Fri May 17 15:50:17 EDT 2002 | davef
Now that�s a switch. Most are moving or properly have moved in the polar opposite direction. Dano, has someone been drilling your teeth lately? We use water washable flux to: * Remove solder balls. [Or put another way, we don�t have to screw-down
Electronics Forum | Thu Jan 10 11:22:48 EST 2013 | pbarton
Looks to me like under etching of the underlying copper and the gold is just plated to all of the exposed copper surface. Is this characteristic the same on all solderable pads? You will not be able to remove this gold.
Electronics Forum | Sat Mar 04 03:48:26 EST 2023 | researchmfg
We had sucessful removed the solder mask by laser machine and got good result and quality without damage the copper layer. You may refer to youtube here by https://youtu.be/cQHaE3_fiqw
Electronics Forum | Wed Jun 30 12:14:40 EDT 1999 | John Thorup
| | We are wave soldering some fabs with a lot of unmasked trace area along the edges. The trace area is solid copper covered with tin / lead, no masking, no components along the edges, same on solder side and component side (goofy board design). I
Electronics Forum | Fri Jul 02 10:06:17 EDT 1999 | John Thorup
| | | | We are wave soldering some fabs with a lot of unmasked trace area along the edges. The trace area is solid copper covered with tin / lead, no masking, no components along the edges, same on solder side and component side (goofy board design)
Electronics Forum | Fri Jul 02 09:54:02 EDT 1999 | John Thorup
| | | | We are wave soldering some fabs with a lot of unmasked trace area along the edges. The trace area is solid copper covered with tin / lead, no masking, no components along the edges, same on solder side and component side (goofy board design)
Electronics Forum | Fri Jul 02 05:28:13 EDT 1999 | Vinesh gandhi
| | | We are wave soldering some fabs with a lot of unmasked trace area along the edges. The trace area is solid copper covered with tin / lead, no masking, no components along the edges, same on solder side and component side (goofy board design).
Electronics Forum | Fri Oct 07 09:18:39 EDT 2005 | russ
If you're using non-lead free parts then you don't have a pbfree assembly so why worry about marking it anyway? We apply this artwork after the assembly has been completely engineered for lead free. Artwork can be covered up with mask or whatever if
winsouce.jpg)