Electronics Forum | Tue Dec 30 20:48:31 EST 1997 | Tom Gervascio
Has anyone had any experience with thermal shocking and cracking of SMD capacitors during the rework process? My company was advised to preheat capacitors to 125 C at a rate of 2 C/sec before replacing them onto boards. Would this maybe degrade c
Electronics Forum | Fri Jun 06 06:11:18 EDT 2014 | paulg
I have a large monoblock ceramic filter on a PTFE based pcb material. The filter has a metal casing soldered onto the ceramic filter. I am concerned that if the heating rate is to rapid, then thermal shock / differential expansion could cause the fil
Electronics Forum | Thu Jan 01 13:04:42 EST 1998 | scott cook
| Has anyone had any experience with thermal shocking | and cracking of SMD capacitors during the rework process? | My company was advised to preheat capacitors to 125 C | at a rate of 2 C/sec before replacing them onto boards. | Would this maybe
Electronics Forum | Sat Jan 03 18:13:58 EST 1998 | David Jacks
Tom: You are right. Pre-heating is just as necessary in rework as it is in intiial production. Zephyrtronics produces an economical convective bottom side pre-heater known as an airbath. This product ramps the substrate and assembly at 2-4 degrees
Electronics Forum | Mon Jun 09 11:11:57 EDT 2014 | cyber_wolf
What does the technical data sheet for the component recommend for reflow profile ? Can you post a photo of the component ?
Electronics Forum | Wed Dec 31 10:09:27 EST 1997 | Ken Daniels
| Has anyone had any experience with thermal shocking | and cracking of SMD capacitors during the rework process? | My company was advised to preheat capacitors to 125 C | at a rate of 2 C/sec before replacing them onto boards. | Would this maybe
Electronics Forum | Wed Dec 31 08:55:09 EST 1997 | justin medernach
| Has anyone had any experience with thermal shocking | and cracking of SMD capacitors during the rework process? | My company was advised to preheat capacitors to 125 C | at a rate of 2 C/sec before replacing them onto boards. | Would this maybe
Electronics Forum | Sun Jan 11 11:28:14 EST 1998 | Bob Willis
Most componnent cracking is mechanicaly produced a guide to causes of capacitor damage is included as a download file on my web page www.bobwillis.co.uk I feel that the supplier is looking to blame some one else. IPC make comment on pre heating chip
Electronics Forum | Sun Jan 11 11:28:12 EST 1998 | Bob Willis
Most componnent cracking is mechanicaly produced a guide to causes of capacitor damage is included as a download file on my web page www.bobwillis.co.uk I feel that the supplier is looking to blame some one else. IPC make comment on pre heating chip
Electronics Forum | Wed Dec 31 23:02:19 EST 1997 | Scott McKee
| Has anyone had any experience with thermal shocking | and cracking of SMD capacitors during the rework process? | My company was advised to preheat capacitors to 125 C | at a rate of 2 C/sec before replacing them onto boards. | Would this maybe
.jpg)