Electronics Forum | Sat Jun 21 23:15:07 EDT 2008 | mika
Also keep in mind that the CCGA column length tolerance is at minimum +/- 0.13mm from most part manufactures and they don't collapse in the same way as a BGA, therefore the paste height deposit could be critical in some rare circumstances. Board warp
Electronics Forum | Tue Mar 15 17:58:56 EST 2005 | darby
Mat, Are you sure you should be using SnPb HASL boards if you are doing prep for lead free? If you aren't actually going to comply with RoHS then fire away. Nearly all of our assemblies are now ENIG and as any re-design comes up on a HASL board it is
Electronics Forum | Wed Jun 14 18:07:11 EDT 2006 | grantp
Hi, Thanks for all the help guys, and we did a bunch of things to get it working. We raised the pump speed, and also went to a water based flux, which helped a lot. We also reduce pre heat as we were burning off the flux. It's doing really nice jo
Electronics Forum | Fri Jun 15 22:00:23 EDT 2007 | grantp
Hi, Thanks for the reply guys, and this is interesting information. I had assumed that if we had a paste spec, and this was the spec for the solder to reflow correctly, then if I achieved that spec, the solder should perform correctly. However this