Electronics Forum | Thu May 31 10:52:31 EDT 2007 | patrickbruneel
A solder wire classified as L0 under IPC J-STD-004 means that the flux residues can be left on the board safely, and when you select this type of cored wire the intention is not to clean. You just select a solder wire that gives you an acceptable lev
Electronics Forum | Fri Jun 25 12:19:52 EDT 2010 | operator
I have always been under the impression that you want the flux make-up of your cored wire and supplemental flux (squeeze bottle) to be as identical/compatible as possible. I was just looking over a manufacturers datasheet for a resin-based cored wir
Electronics Forum | Fri Jun 25 14:49:43 EDT 2010 | patrickbruneel
Just skip the squirt bottle and your problem is solved. Cored solder has enough activity for proper wetting. When occasionally extra activity is needed use a fluxpen.
Electronics Forum | Mon Feb 18 17:36:32 EST 2008 | kennyg
I should have mentioned... the only flux we use for the hand soldering is wire-core, no bottle flux. I think it should be a non-issue to leave the activated wire core flux residue. I'm just looking for some way to prove it to the designer.
Electronics Forum | Fri Jun 01 17:31:17 EDT 2007 | gsala
Thanks Patrick, also IPC-HDBK-001 explains even better then IPC-J-STD-004, but unfortunately not yet infos about flux for L-F soldering.That's why I am trying to get some infos more from experienced people. Some L-F (SAC or SACX) cored wires vendor
Electronics Forum | Mon Mar 25 21:45:22 EDT 2024 | buckeye
I got an inquiry from one of our electronics labs with regards to their soldering processes. They use eutectic (63% Sn, 37% Pb) solder. For liquid flux they are currently using Kester 186, which is an old-school, full rosin (RMA and ROL1) flux that c
Electronics Forum | Mon Apr 17 19:46:39 EDT 2000 | Dave F
Murad: Your customer is smart to be concerned about the affect of changing production processes on product reliability. Your Company is smart to inform customers and keep them in the loop about these changes. In developing your demonstration of th
Electronics Forum | Tue Apr 14 15:42:45 EDT 1998 | Scott Cook
| Scott, | I am not really in a position to answer this as fully as I would like because most military work with which I am familiar is subject to some degree of secrecy most especially on the internet. At least we have signed up to such restrictions
Electronics Forum | Wed Apr 08 18:15:18 EDT 1998 | Graham Naisbitt
Scott, I am not really in a position to answer this as fully as I would like because most military work with which I am familiar is subject to some degree of secrecy most especially on the internet. At least we have signed up to such restrictions. Ho
Electronics Forum | Thu Jul 25 12:25:54 EDT 2019 | davef
In “J-STD-001 Rev G Amendment 1 Process Qualification” Debbie Carboni, Global Product Line Manager, KYZEN Corp, Nashville, TN said: What change constitutes a need for requalification? Major/ Level 1 – Flux or flux-bearing materials (e.g. flux, so