Electronics Forum | Thu Oct 08 12:11:34 EDT 1998 | Rick Wyman
| Does anyone know of an AOI system that can look at the solder joints of SMT chip devices (1206,0805 & 0603) and make a reliable presence/abscence call of the joint on a HASL PCB. A low false call rate (much less than 1%)is required. Any info. fro
Electronics Forum | Thu Jun 17 21:31:06 EDT 1999 | Dave F
| | Does anyone know where I can find a list of things to do to when troubleshooting issues during the wave solder process? | | | | for example: | | | | Solder Bridge | | 1.verify amount of flux been aplied. | | 2.verify turbulance on your solder w
Electronics Forum | Thu Sep 30 03:17:45 EDT 1999 | Brian
| Hi everyone, | | Greetings! | | I�ve got a 2-layered through-hole PCB�s having the following problems: | | Solder Mask peels after wave soldering at random locations and only at the bootom side of the PCB | Insufficient Solder and some solder ne
Electronics Forum | Thu Jul 20 14:52:05 EDT 2000 | Bob Willis
If you are talking about Pin In Hole Reflow that is not true, I hope it was not my friends at Speedline that told you that. Stencil printing of paste for through hole reflow can be done. If you get all the parameters right it can give you joints lik
Electronics Forum | Thu Jun 17 22:10:48 EDT 1999 | Earl Moon
| | | Does anyone know where I can find a list of things to do to when troubleshooting issues during the wave solder process? | | | | | | for example: | | | | | | Solder Bridge | | | 1.verify amount of flux been aplied. | | | 2.verify turbulance on
Electronics Forum | Fri May 14 14:52:56 EDT 1999 | Ryan Jennens
| | | | I am looking for anyone who has converted over to VOC Free flux. I need some info on any problems, etc. that you might have had. | | | | | | | | Please E-mail me at wes.ruggles@vickers-systems.com or call at (513) 494-5229 | | | | | | | | T
Electronics Forum | Fri Feb 24 13:04:17 EST 2006 | patrickbruneel
Hi All, The change over to lead-free is as easy or as difficult as you want to make it The big problem I see with this lead-free transition is that there is no benchmark of acceptability and no defect data (yet) related to visual appearance of a sol
Electronics Forum | Tue Sep 20 11:59:06 EDT 2011 | SheanDalton
Check specific gravity: According to a quick web search, the specific gravity should be 0.813 ± 0.003. If you have records of the specific gravity, compare current reading to past readings. Check pressure near stone: if you have records, compare
Electronics Forum | Fri Jan 06 00:03:10 EST 2023 | SMTA-64419298
Hello Evtimov, sorry...just saw post as I was looking through list...a bit late. I don't know if you ever got your answer. IPC-4552A covers EniG finishes and suggested shelf life. I've referred to these doc's quite a bit. Good spec's ! Yes, I beli
Electronics Forum | Fri Jun 04 10:02:06 EDT 1999 | Chrys Shea
| | I'm encountering a new problem at my new company that I haven't encountered before in my past life - and that's Wave Soldering VIA holes. | | | | We've been getting a rash of defects that we call in this company, "insufficient solder in VIA hole