Electronics Forum | Thu May 30 10:31:03 EDT 2002 | robbied
Hi Yannick. This is an issue that we are just recently getting into but here is some ifo that I have gathered so far. I have seen/ used 2 different rework machines. The one we have bought is a 'PACE TF2000' which was at the lower cost end of the mar
Electronics Forum | Mon Nov 09 09:44:22 EST 2015 | davef
Purpose. This describes setting-up a wave soldering system set-up for a new assembly design or checking a wave solder machine operation with a test board. Applicability. To be used for new design printed circuit assembles and during machine accept
Electronics Forum | Sun Nov 08 15:27:25 EST 2015 | davef
Thinner: Flux thinner, NOT paint thinner We kept a spare stone in thinner in inventory. We cut PVC pipe to size, cap in one end, screw thread on the other, stone inside, filled with flux thinner and covered with a screw cap. I don't remember who we
Electronics Forum | Fri Jan 22 15:48:14 EST 1999 | Chrys
| Hello, | | I will be evaluating and qualifying two equipment types. The first is a fountain soldering device. I need practical advice on all the stuff you guys and gals know about as good, bad, ugly, best applications, setup, limitations, and all
Electronics Forum | Thu Apr 19 20:01:30 EDT 2012 | eadthem
some things to consider, Is there flux on the board. are there finger prints on the tops of parts. Is the board warped at the V score from reflow Is the board shifting in the machine during inspection. These are the issues we have had with our mir
Electronics Forum | Mon Apr 09 11:34:59 EDT 2018 | emeto
definitely don't mix clean and No clean. Run No Clean as you decided, but have your flux and paste manufacturers advice, how this flux can be cleaned(if you decide or required to clean). I know for a fact that some of these NC flux residues are almos
Electronics Forum | Fri Apr 06 12:31:07 EDT 2018 | deanm
Your fluxes are required to be compatible per J-STD-001. I wouldn't even attempt mixing no-clean (rosin) and clean (assuming water soluble) fluxes on the same assembly, especially if the fluxes are from two different vendors. If your paste and liquid
Electronics Forum | Mon Aug 24 07:32:34 EDT 2009 | hurr
Hi Joane, this flux is primarily designed for wave soldering. I think that manual soldering it´s possible. Certainly it´s very hard to dispensing correct amount of the flux. Succinic acid is one from all ingredients of this flux. If you have this
Electronics Forum | Thu Oct 11 19:31:58 EDT 2007 | davef
We'd probably hand solder these coils with low residue fluxed wire solder, after cleaning.
Electronics Forum | Thu Jul 06 12:26:55 EDT 2006 | Chunks
Sounds like your flux to me. Since you cannot change the board or the machine, changing flux would be one question mark you could take away with a phone call and a sample. You will really be surprised how different fluxes can affect your final prod