Electronics Forum | Thu Nov 12 11:16:55 EST 1998 | Dave F
| | | I have a need to dispense a latex masking material using an automated dispensing system. We are presently looking at the I&J750. Does anyone have any experience with this piece of equipment, or have a better solution available? | | | | | Dou
Electronics Forum | Fri Nov 13 10:25:11 EST 1998 | Doug Clement
| | | | I have a need to dispense a latex masking material using an automated dispensing system. We are presently looking at the I&J750. Does anyone have any experience with this piece of equipment, or have a better solution available? | | | | | |
Electronics Forum | Fri Jul 16 19:31:18 EDT 1999 | Scott McKee
| I'm planning to introduce selective point-to-point soldering for pwb. This is due to various needs: PIHs assy on double IR, for example. I think the most suitable solution is a point-to-point soldering, 'cause we're still having small lot/many type
Electronics Forum | Fri Jul 16 14:42:36 EDT 1999 | Glenn Robertson
| I'm planning to introduce selective point-to-point soldering for pwb. This is due to various needs: PIHs assy on double IR, for example. I think the most suitable solution is a point-to-point soldering, 'cause we're still having small lot/many type
Electronics Forum | Tue Jul 20 11:33:55 EDT 1999 | Ted Kress
| | I'm planning to introduce selective point-to-point soldering for pwb. This is due to various needs: PIHs assy on double IR, for example. I think the most suitable solution is a point-to-point soldering, 'cause we're still having small lot/many ty
Electronics Forum | Wed Jul 27 09:58:05 EDT 2011 | davef
Pressure printing systems Conventional stencil printing techniques have fundamental limitations as regards paste handling: The volume of paste available for printing is limited, so frequent replenishment is necessary Paste is difficult to c
Electronics Forum | Thu May 09 12:06:06 EDT 2013 | pbarton
We run Zipatec 460's also. I presume that you are running Nitrogen? We have found that if the Nitrogen flow rate is too high into the conical nozzle collar it can be sufficient to disrupt the smooth flow of the solder as it runs down the wettable o
Electronics Forum | Wed May 03 11:12:08 EDT 2006 | samir
Iron huh? You sure about that? We have the ERSA Versaflows and our nozzles are made out of ST37 Tool Steel. There is an "American equivalent" to this grade but I forgot what it is. You'll have to google it like I did. Anywho, Tin or Tin-Lead sold
Electronics Forum | Thu May 04 10:29:40 EDT 2006 | Chunks
"Bending nozzles" "Changing dwell times" "Navels" (!!!!!!!!!??????????) And probably not taking responsibility when the poop hits the fan cause "you're just an operator". Not knowing your boards, but estimating your time scenario, I'd say you're sol
Electronics Forum | Tue May 02 14:30:07 EDT 2006 | finalassy
We have recently bought two new Pillarhose Jade selective soldering units. We are having a extremley hard time keeping the nozzels wetted while running the machine. I know that the nozzels are 99 percent iron. Has anybody ran into this problem, if