Electronics Forum | Sat Nov 09 08:04:52 EST 2002 | erhard
if you wave solder you have to glue the SMD parts on the bottom side. If you reflow the bottom side then you usually shouln't go over the wave afterwards. It's quite logical the joints melt again, that's what you want to achieve going over the wave.
Electronics Forum | Sat Nov 09 15:13:06 EST 2002 | mjabure
If I understand what you're saying, you are reaching reflow temp's on the top side while soldering bottom side components. You might want to run a glass gauge plate over the wave and make sure your contact pattern isn't too large. If your PCB is in c
Electronics Forum | Fri Nov 08 18:36:31 EST 2002 | leeloo
Nowadays I have a problem, I am in chsrge of the section of smt in my company, have a normal process inside my department with a minimal level of mistakes, the problem happens when the material is liberated to the lines of production on happened for
Electronics Forum | Mon Nov 11 11:42:26 EST 2002 | MikeF
Like Mark, I'm guessing your problem is with SMT parts on the top side, the solder is re-melting and some of the parts are moving around during when the board is being wave soldered. When I had some training on thru hole wave soldering way back when
Electronics Forum | Mon Dec 20 08:26:17 EST 1999 | pascal MATHIEU
hello guys ; we are using some standard selective wave soldering unit used in lined ; the drawback of a such machine is 1/the speed which is quiet low (the board is coming on position through the conveyor, then the head delivering the solder moves s
Electronics Forum | Fri Apr 04 09:54:39 EDT 2008 | redtiger56
We have been seeing continued difficulty with solder shorts and/or insufficient barrel fill with our Juki selective solder machine while using SAC305. We want to switch to something in the SN100 series, but we do not know enough to seperate the hype
Electronics Forum | Sun Jan 01 22:48:46 EST 2006 | Joseph
We are using selective soldering pallet, which the soldering flux is Interflux 2005M. We encountered the poor hole fill mainly at the heat sink components. Initially we tried to apply more heat but tend to overkill the flux activity. After some modif
Electronics Forum | Thu Dec 29 09:20:30 EST 2005 | Cmiller
We have tested SN100C and SAC305 in our selective solder machine (Ersa Versaflow). We wanted to test both alloys in the selective first because the investment in filling the pots is minimal. In our initial tests the SN100C alloy appears to be the bes
Electronics Forum | Wed Jul 30 16:16:19 EDT 2003 | swagner
What is the industry standard for wave and selective solder PPM defect rate for a world class facility, any responses are appreciated.
Electronics Forum | Wed Jul 30 16:42:24 EDT 2003 | davef
here's a start http://www.thepdfshop.co.uk/ppm/asp/Monthly.asp