Electronics Forum | Fri Dec 29 16:38:15 EST 2017 | mekmat544
Hello all, I would like to ask you about difference between wettable and nonwettable solder nozzle: Are there some pros and cons for each type? Thank you. Mekmat
Electronics Forum | Fri Nov 14 10:40:35 EST 2014 | eniac
I use a two machines from EBSO, Germany. It's a machines with PCB carrier, so, solder pot is fixed. I'm fully satisfied with this equipment, but I use only wettable nozzles. If you would like to buy a new machine, not in used condition, EBSO will be
Electronics Forum | Tue Aug 16 15:39:07 EDT 2011 | mwest
What type of coating is used on the Vitronics selective solder nozzles? Any help?
Electronics Forum | Thu Aug 18 10:37:37 EDT 2011 | tombstonesmt
We do not use a Victronics selective solder but we you activ8 102 stainless steel flux from worton metals for our nozzles. Hope this helps.
Electronics Forum | Mon Nov 10 08:53:23 EST 2014 | jpal
We have the opportunity to buy a new selective solder machine and are used to using a very old Jade machine with a moving tank and wetted nozzle. I have two process concept questions: Which is better- move the board over the nozzle or move the nozz
Electronics Forum | Thu Nov 13 12:49:45 EST 2014 | dyoungquist
I have no experience running a "move the board" selective solder so can not compare the 2 methods..... We have been using an RPS Rhythm "move the pot/nozzle" system since 2008. We are using it solder thru hole components onto boards that often have
Electronics Forum | Fri Mar 22 14:19:38 EDT 2019 | gregcr
Thank you ProcEng1 Nordson sent me a flux suggestion list: No Clean: 1. Kester Select 10 2. ALPHA EF-2210 3. AIM FX-16 Water Sol: KESTER 2331-ZX Nozzle Tinning: SUPERIOR #75
Electronics Forum | Mon Nov 10 09:03:47 EST 2014 | rgduval
I can't claim to be an expert....I've just bought a used RPS, and it'll be my first...but, after reading through their manual, and working on setting things up, I'd say: -Conceptually, I like the idea of moving the board rather than moving the entir
Electronics Forum | Fri Jun 23 12:54:53 EDT 2017 | guts1872
We are having issues with top fill and dropping pins on Molex connectors with our KISS 101. Unfortunately we do not have a pre heater and bottom side pre heat with our nozzles is not satisfactory. Most of the issues occur when using a no clean proces
Electronics Forum | Fri Apr 28 10:50:26 EDT 2017 | emeto
Hello experts, Here is my problem: I have a board that has smt parts on one side and TH parts on the other. We designed special pallet for wave, but the pallet itself is 15mm thick, so we are still seeing some defects. Have any of you tried to find