As far as hole fill, as was stated above, class 2 only requires 50% up-fill. In order to get better up-fill on the initial pass, you may need to consider more pre-heat. Also, better application of flux. Are you using a drop jet, or a spray? You
Electronics Forum | Thu Jun 03 17:43:34 EDT 2004 | g2garyg2
Hi Doug, Read your inquiry. My company PRO-MATION has some exciting technologies available for both top side and bottom side selective laser soldering. Our work cells are great for low volume / high mix environments and are capble for both Tin Lead
Electronics Forum | Fri Jun 23 12:54:53 EDT 2017 | guts1872
We are having issues with top fill and dropping pins on Molex connectors with our KISS 101. Unfortunately we do not have a pre heater and bottom side pre heat with our nozzles is not satisfactory. Most of the issues occur when using a no clean proces
Electronics Forum | Thu Jun 29 12:07:09 EDT 2017 | georgetruitt
HOW THICK IS THE BOARD? IS THERE A LOT OF COPPER IN THE BOARD? DOES YOUR CUSTOMERS PROVIDE HEAT RELIEF IN THE BOARDS BARREL DESIGN THERE NEEDS TO BE PLENTY OF ROOM FOR LEADFREE SOLDER TO FLOW, DID YOU CHECK YOUR PIN(LEAD)TO HOLE (BARREL) RATIO? N
Electronics Forum | Mon Dec 10 13:26:40 EST 2012 | dyoungquist
We are using our selective solder machine to solder a backplane with sixteen (16) 4x48 pin 0.080" connectors. Our first pass yield is about 85% meaning that 85% of the connectors come out with no bridges. Not quite as fine pitch as your connector a
Electronics Forum | Tue Dec 16 09:01:52 EST 2003 | tds
What model is your Hollis? Does it have the coil heater?
Electronics Forum | Tue Dec 16 21:17:48 EST 2003 | Peter
Maybe you fixture is too large for your product. If so, please redesign your fixture
Electronics Forum | Wed Dec 17 06:50:51 EST 2003 | ex maintain leader
140..155 degrees celsus the limit is your inserted component temp schock tolerance
Electronics Forum | Tue Dec 16 06:42:51 EST 2003 | Kev
I am having problems achieving correct pre-heater temperatures with our Hollis solder wave. Our original "Verification Golden board" program uses a conveyor speed of 5ft per minute and pre-heat temps of 300, 350, 400 respectively. Our "golden Board"