Hi Doug, Read your inquiry. My company PRO-MATION has some exciting technologies available for both top side and bottom side selective laser soldering. Our work cells are great for low volume / high mix environments and are capble for both Tin Lead
Electronics Forum | Wed Nov 02 11:14:45 EST 2005 | Doug
I am doing lead free testing on a Vitronics selective machine with a 4 mm nozzle. The finishes I am testing are ENIG, ImSn, and ImAg. The problem I am encountering is achieving good top side wetting. Has anyone had any luck with this type of an ap
Electronics Forum | Wed Aug 30 21:44:56 EDT 2006 | IRAS
HI, I am looking for the smallest wave soldering machine available. So far I have found some that have a total of 8 feet in length, and a foot print of 5.5 feet wide. Is there a wave solder smaller than this?
Electronics Forum | Thu Aug 31 08:37:39 EDT 2006 | nodlac
um why? Technical Devices = 5'8"
Electronics Forum | Wed Jul 04 11:55:23 EDT 2012 | tony_d
We are a low to mid range manufacturer as well. I looked at several different vendors incuding; Mirtec, Viscom, Marantz, Omron, VI Tech, Orbotech and Yestech. We selected Mirtec. As a mid range manufacturer, one of my main concerns was quick and eas
Electronics Forum | Mon Apr 18 12:14:39 EDT 2022 | proceng1
As far as hole fill, as was stated above, class 2 only requires 50% up-fill. In order to get better up-fill on the initial pass, you may need to consider more pre-heat. Also, better application of flux. Are you using a drop jet, or a spray? You
Electronics Forum | Wed Dec 12 16:16:39 EST 2012 | tombstonesmt
Nitrogen at nozzle supply is at around 47.5cfh.
Electronics Forum | Mon Dec 10 13:26:40 EST 2012 | dyoungquist
We are using our selective solder machine to solder a backplane with sixteen (16) 4x48 pin 0.080" connectors. Our first pass yield is about 85% meaning that 85% of the connectors come out with no bridges. Not quite as fine pitch as your connector a
Electronics Forum | Mon Sep 24 18:03:43 EDT 2012 | rmazenha
Hi, i am using AIM 264-5 No Clean flux for soldering alpaca pieces on PCB boads, but i am having problems: poor filling and no solder. I am using SAC 305 lead free solder. I have tried to change flux pressure, time, ammount as well solder speed an
Electronics Forum | Mon Mar 17 04:31:52 EDT 2008 | d0min0
Hello, tried searching the SMTnet archives, but not yet a clear answer - maybe there is not a one yet ? ;) last discussion I found is few years old so maybe there is a fresh view on that? Q: we want to prove that our proces is "clean" we use SAC30