Ben- My understanding of Tacky Flux is for Automation process where the Tacky Flux helps hold the component in place. If you are using a rework system that holds the Board firm..then typical no clean flux (Flux Pen) should work fine. I can only asum
Electronics Forum | Thu Jan 20 09:49:08 EST 2005 | Mike Konrad
Regarding the reference (Patrick) to a previous thread promoting �no-residue� fluxes, I must say that there is absolutely no such thing as �No-Residue� flux. There are �Low-Residue� fluxes and even �Very-Low� residue fluxes but to suggest that there
Electronics Forum | Thu Sep 06 10:34:21 EDT 2001 | Mike Konrad
Hi Jeff, Sean is correct. Although ultrasonic technology will work in post-reflow de-fluxing applications, you will receive concerns regarding ultrasonic �damage� to wire bonded components. Much has been written to combat this belief but the conce
Electronics Forum | Wed Feb 26 23:59:48 EST 2003 | Mike Konrad
Grant, No-Clean paste + IPA = White Residue! #1: Stop using IPA #2: Switch to either a solvent-based de-fluxing chemical or an aqueous-based de-fluxing chemical. If you are using an ultrasonic cleaner for your boards as stated, do not use sapon
Electronics Forum | Mon Oct 02 20:28:25 EDT 2006 | davef
Assuming: * Customer board has been designed to provide for cleaning under components. * Cleaning equipment is capable. In meeting J-STD-001, your current cleaning equipment should be able to clean: * Water washable fluxes. * Low residue fluxes, pro
Electronics Forum | Wed Jun 25 09:51:51 EDT 2014 | iam09
Hi Sirs, We are running Tin Lead process and we have boards that required clean and no clean process which have different flux application in our wave process. We are looking into opportunity to use common flux system for both clean and no clean an
Electronics Forum | Fri May 04 08:23:17 EDT 2001 | Dave Brady
No titration is needed for a fluxer that has a closed flux flow system such as a Opti fluxer. The flux is fed from a pressurized vessel directly to the applicator with no evaporation or change in the flux composition. I hope this helps. If you need
Electronics Forum | Wed Sep 15 05:15:24 EDT 2004 | Adam
I have chceked the fluxing application, I seem to be getting good consistent coverage across the board using our foam fluxing system. Good flux penetration on the top-side of the through-hole plating, as this was checked using a fax paper.There is no
Electronics Forum | Tue Jun 16 07:52:50 EDT 1998 | Jim Zanolli
| can any body help on assembling straddle mount connectors on to a board? for information on the connector - it is a berg micropak connector Teka Interconnection Systems (http://www.tekais.com)manufactures straddle mount connectors with solder and
Electronics Forum | Wed Mar 22 14:46:54 EDT 2017 | solderingpro
Laser Soldering by nature is a very dialed in process. - Requiring specially formulated flux and solder paste applications that will perform while absorbing a massive amount of energy. What I believe "Gary" is attempting to say is: Laser Soldering c