Electronics Forum | Mon Aug 28 12:41:35 EDT 2000 | JAX
MoonMan, I'll take a crack at the list. Feel free to answer the ones I don't! 1. Solderability is a parameter which indicates how well a component can be soldered. As far as Solder Termination Coatings go, here are some up�s and down�s of a few. Ha
Electronics Forum | Fri Aug 20 17:17:14 EDT 1999 | K.T
| | | | Yesterday as I was creating a profile on a plastic BGA using Conceptronics freedom 2000 rework station, I happend to discover that I was able to remove solder bridging from a plastic BGA. | | | | | | | | This is what I did. | | | | | | | |
Electronics Forum | Wed Jun 16 12:43:10 EDT 1999 | Brian
Cliff, I'm sending you by e-mail (don't think I can attach a graphics file here) the doc proof that the problem lies between Atlanta and Ft Lauderdale. This was an attempt to trace your routing. From Cyprus, it crossed the Atlantic by West Orange. U
Electronics Forum | Mon Aug 16 20:19:10 EDT 2004 | Grant
Hi, We have both Vapor Phase ASSCON semi auto as well as Soltec convection inline ovens. I must say we had no end of problems with Vapor Phase. We tried everything, and just could not totally eliminate tomb-stoning completely. We would always get a
Electronics Forum | Wed Nov 04 11:35:01 EST 2009 | dilogic
1. can you load cut tape onto the feeders, or only reels? You can, but you have to use cover tape extender (pretty cheap, though) >2. how about parts on trays (like Atmel AVRs in the QFP package)? You need tray feeder. But you can "make" your own
Electronics Forum | Wed Nov 13 04:12:20 EST 2013 | hqew2013
Do you design or define PCB layouts? If so circuit board, what rules and checks do you have in place to make sure your results are... optimal? Over the years, I've created a PCB design checklist to keep me out of trouble. I share these nuggets with m
Electronics Forum | Fri Jan 19 17:43:30 EST 2001 | davef
Intermetalic Layer (IL). A compound formed at the interface of two different metals, whose atoms have an extremely high natural attraction for each other, so high, that they do not bond to other elements by any other means. Also, intermetalic compo
Electronics Forum | Mon Oct 30 16:00:30 EST 2000 | Finepitch Services
Sal, I kind of assume you have paste there to start with... Because sometimes the edge components do not have paste applied caused by the bottom support in the screen printer etc. And if that is the case for one direction, the other direction applie
Electronics Forum | Wed Aug 23 08:32:32 EDT 2000 | Earl Moon
Well Sun, This is Moon and you are out of phase with reality. I have nothing against advertising as long as it does not prohibit free technical intercourse as it did me and the investment I made several years ago. Free my ass. I mean, let them make
Electronics Forum | Wed Nov 01 12:10:20 EST 2000 | Jeff
charles, i can appreciate the hand held "reel to reel" scanner as a good solution that is very cost effective. during my smt supervision days we had a number of part loading checks. 1. load plan check, 2. scan check, 3. reel to reel manual check.