Electronics Forum | Tue Jun 16 09:15:56 EDT 1998 | Justin Medernach
| We are very concerned about microcracking in SMT P&P process. I want to know something about: | What is microcracking? | When did it occur? What are the causes? | How can avuid this phenomena? Toni, Micro cracks can be caused by a ton of conditions
Electronics Forum | Wed Jun 10 18:50:36 EDT 1998 | Earl Moon
| | | Does anyone have any info./studies on what the percentage or PPM defect rates are for each part of the typical SMT process. | | | Example: | | | Screen Print = 45% of total defects | | | Component Placement = 25% of total de
Electronics Forum | Tue May 19 12:54:55 EDT 1998 | Richard Jackson
| We had a similar problem. But whenever the solder came from the screen printer the solder would wet to the gold fingers, with the help of residual flux. But the problem is balls, that I assume are not wetted to the gold fingers but instead are jus
Electronics Forum | Mon May 18 20:57:06 EDT 1998 | Earl Moon
.025" pitch so the only problem we run into is too much HASL on the adhesive side causing improper glue dispense. | As Earl keeps saying HASL thickness is hard to impossible to control. I think we need to look hard at OSP's again but then you get in
Electronics Forum | Mon May 18 22:54:04 EDT 1998 | Dave F
.025" pitch so the only problem we run into is too much HASL on the adhesive side causing improper glue dispense. | | As Earl keeps saying HASL thickness is hard to impossible to control. I think we need to look hard at OSP's again but then you get
Electronics Forum | Fri May 15 19:06:34 EDT 1998 | Steve Abrahamson
We are looking to bring in a HP 5DX System. This is the laminography equipment formerly known as Four Pi. I have our sales rep getting us a few references, but I wanted to get some opinions from the tech net. I am looking for input from someone wh
Electronics Forum | Tue May 05 13:44:57 EDT 1998 | Mark Mitchell
Mr. Desrochers; Philips EMT Americas offers a three day course entitled, "Introduction to SMT Manufacturing". The course addresses all major factors that influence the automated SMT assembly process. Topics that are discussed in the course are list
Electronics Forum | Wed Apr 29 17:01:38 EDT 1998 | Wayne Bracy
Steve: Can't say that we do everything the proper way, but when possible, we do go the extra mile. I do not think it should make a difference if your are on the East or West side of the country, what matters is that the personal contacts are strong
Electronics Forum | Thu Apr 16 13:40:08 EDT 1998 | Chrys
| Is there anybody to help me ? | We have small balls appearing on the boards soldered by | wave soldering machine and it looks that use of nitrogen | is linked to the problem (because without nitrogen, we have no more | problems). | That remind you
Electronics Forum | Mon Apr 13 07:55:48 EDT 1998 | justin medernach
Dear Justin, I am not asking for experiences with ovens as to whether you think they are capable of THT reflow. I am asking more specifically about actual req's and experiences with THT reflow, regardless of the oven used. Your answer does not hold i