Electronics Forum | Mon Aug 07 08:33:11 EDT 2017 | abruno1995
The vias are filled with the silver plating, it's excess plating and i wanted to know if there was any issues with ICP
Electronics Forum | Tue Apr 28 04:06:25 EDT 2015 | anirudh_thabjul
thankyou for your answer. I came to know that "ENIG/ENEPIG is much costlier than Immersion Silver and Immersion Tin. So, my company doesn't allow me to use ENIG/ENEPIG". So, i will suggust my company to use Immersion silver or Immersion tin. Rega
Electronics Forum | Thu Apr 27 10:35:21 EDT 2000 | Russ
Scott, I am a little confused, when you mention "silver thru hole vs. plated through hole what do you mean. A silver "immersion" type finish vs. HASL (Tin lead)on your PCB? Or are you talking about using silver solder to perform intrusive reflow of
Electronics Forum | Thu Jan 17 14:52:17 EST 2008 | gnath
All, Can someone help find a source for purchasing interleaving/packaging paper for Immersion Silver boards (sulfur free + ph neutral ..). Thank you!
Electronics Forum | Tue Aug 25 11:19:00 EDT 2015 | cyber_wolf
Adam, We have very recently experienced poor wetting on immersion silver as well. I would be very interested to talk to you offline, however I do not see the option to private message forum members.
Electronics Forum | Fri Aug 04 08:32:07 EDT 2017 | abruno1995
So i am a quality inspector and i am having issues with the immersion silver PCB. I have found the via holes to be somewhat filled and i wanted to know if anyone knew it this is a CLASS 1, 2, 3, ICP DEFECT or what it is at all?
Electronics Forum | Sun Jun 06 09:20:03 EDT 2004 | michaeljm
My department and I have been working with immersion silver on and off for about four years and we have compiled quite a bit of data for the Alpha and MacDermid immersion silver chemistries. We have not encountered any assembly or storage related is
Electronics Forum | Fri Feb 21 20:41:32 EST 2003 | Raul
It is a common knowledge that sulphur and immersion silver finish on a PCB do not go together very well. We are seeing peaks of sulphur on some of our assemblies (with silver finish) and as expected we experience severe difficulties with processing t
Electronics Forum | Fri May 24 07:09:52 EDT 2002 | Andy Hoggan
Teh amount of silver on an immersion silver board won't effect 62/36/2 tin/lead/silver solder, however if the silver on the board is on the thick side and you have a high trace silver content in a 63/37 tin/lead then with the combination of the two y
Electronics Forum | Mon May 13 16:20:10 EDT 2002 | ian
Are you refering to MacDermid Sterling Silver finish or immersion silver in general. We have had enquiries about Sterling Silver from a customer and the blurb I have read looks very good (don't most sales literature). Has anyone tried this finish? O