Indy, We use Palladium silver surface finish parts for silver epoxy attached parts only. It is our understanding that this finish is not for solder, but only silver epoxy attach. I expect that is you problem. Dave
Electronics Forum | Thu Apr 29 18:48:11 EDT 1999 | Kiet Dang
Hi, Did anyone experience a problem with electrically conductive silver filled epoxy is resistive due to galvanic reaction? I'm having this problem when attaching components to Ni plated housing while conducting an experiment to cost reduction for Au
Electronics Forum | Sun Jul 04 19:49:05 EDT 2004 | indy
Hello Everyone, We are having some problem with Palladium-Silver surface finish. We have ceramic components with the above surface finish. When we try to assemble these on Sn/Pb solder, we are observing open joints. If we reflow the compt for more t
Electronics Forum | Thu Aug 12 18:06:09 EDT 2004 | SR
May I ask what component types you are using and who the suppliers are? FYI - If the components have exceeded their shelf life, they may have oxidized too much for soldering using low activity fluxes. Thanks and best regards, SR
Electronics Forum | Tue Jul 13 16:35:25 EDT 2004 | Richard
Sounds like your Si plalladium finish has oxide on it from the firing or sitting around too long. I used to assemble LTCC and have had plenty of dealings with this matter. The best and easiest is to get an active type flux and solder paste. AIM makes
Electronics Forum | Thu Oct 18 18:39:15 EDT 2001 | davef
Responding to your questions ... RELIABILITY OF 1% SILVER SOLDER PASTE: It�s as good as the next solder paste, all other things the same. Look at your back articles by Jennie Hang in SMT magazine. I want to say she wrote an article on the topic i
Electronics Forum | Fri Aug 13 16:54:20 EDT 2004 | davef
If the terminations on your components are not barrier plated, you must be very careful about the amount of time you stay above liquidous. As you'd expect, longer is not better. The longer you stay at liquidous, the more of the component terminatio
Electronics Forum | Wed Apr 18 08:14:20 EDT 2007 | davef
Silver palladium termination * AgPd-terminated capacitors are designed for conductive adhesion. Reflow or wave soldering is not recommended. [EPCOS Multilayer ceramic capacitors, Soldering directions, October 2006] * CONDUCTIVE EPOXY BONDING. Epoxy c
Electronics Forum | Thu Sep 10 09:47:15 EDT 1998 | Earl Moon
| hi, | 1206 capacitor with silver/palladium termination is mounted onto a ceramics substrates. Bonding is achieved through conductive epoxy. | We discovered that the epoxy cracked and this caused missing capacitor. We had tried different grade of e
Electronics Forum | Wed Sep 09 21:20:26 EDT 1998 | Simon Ting
hi, 1206 capacitor with silver/palladium termination is mounted onto a ceramics substrates. Bonding is achieved through conductive epoxy. We discovered that the epoxy cracked and this caused missing capacitor. We had tried different grade of epoxy,