Electronics Forum | Mon Jan 29 06:44:59 EST 2001 | Scott B
I have recently come across a device which has a palladium over nickel finish which when soldered shows evidence of poor wetting to the lead ( i.e. a wetting angle greater than 90�) about three quarters of the way up the side of lead. This is only vi
Electronics Forum | Thu Aug 12 20:32:44 EDT 2004 | usdigital
Indy, We use Palladium silver surface finish parts for silver epoxy attached parts only. It is our understanding that this finish is not for solder, but only silver epoxy attach. I expect that is you problem. Dave
Electronics Forum | Fri Aug 13 16:54:20 EDT 2004 | davef
If the terminations on your components are not barrier plated, you must be very careful about the amount of time you stay above liquidous. As you'd expect, longer is not better. The longer you stay at liquidous, the more of the component terminatio
Electronics Forum | Thu Oct 18 18:39:15 EDT 2001 | davef
Responding to your questions ... RELIABILITY OF 1% SILVER SOLDER PASTE: It�s as good as the next solder paste, all other things the same. Look at your back articles by Jennie Hang in SMT magazine. I want to say she wrote an article on the topic i
Electronics Forum | Thu Jun 08 11:37:44 EDT 2017 | jkitt84
davef, thanks for feedback. I talked with a plater who said they put copper before silver when plating brass. Would a complete stack of: Brass part, then 0.0001-0.0002" of copper, then 0.0005" of silver, then Tarniban anti oxidation. Sound reasonabl
Electronics Forum | Thu Jun 08 09:43:42 EDT 2017 | davef
You know the scary part about your mentioning a tread where I post something? Well. let's just say that 2007 was a long time ago. Anyhow, silver will dissolve into your solder and provide no barrier. Some people apply a silver flash plating over the
Electronics Forum | Wed Feb 25 16:39:29 EST 1998 | Eldon Sanders
I agree with Chrys, get the spike temp up and wetting is not a problem. However, when the palladium mixes in with the solder the joint will become more brittle. You need to make sure enough solder is printed on the board to minimize the concentrati
Electronics Forum | Wed Apr 18 08:14:20 EDT 2007 | davef
Silver palladium termination * AgPd-terminated capacitors are designed for conductive adhesion. Reflow or wave soldering is not recommended. [EPCOS Multilayer ceramic capacitors, Soldering directions, October 2006] * CONDUCTIVE EPOXY BONDING. Epoxy c
Electronics Forum | Thu Aug 07 10:02:10 EDT 2008 | eyalg
We are facing low quality due to soldering opens with coilcraft inductors 0402CS-2N7XGLW. The termination used is(suffix L =RoHS compliant silver-palladium-platinum-glass frit. Did anyone had this problem in the past? Can we do better using T = RoH
Electronics Forum | Mon Mar 30 08:11:22 EST 1998 | Derek Drabenstadt
Does anyone have any experience with fired-silver/platinum/palladium lead terminations soldering. I have had issues on nickel over gold plated boards but not with HASL'd boards with tin/lead pads. Is this the norm?