Electronics Forum | Thu Apr 20 14:08:34 EDT 2006 | cw
hi All, recently i have received some parts with the lead turning black, and i then found out the leads are silver plating, is that going to be a problem? or it is simply a cosmetic issue? pls advise ASAP!! thansk a lot!!
Electronics Forum | Wed Apr 18 08:14:20 EDT 2007 | davef
Silver palladium termination * AgPd-terminated capacitors are designed for conductive adhesion. Reflow or wave soldering is not recommended. [EPCOS Multilayer ceramic capacitors, Soldering directions, October 2006] * CONDUCTIVE EPOXY BONDING. Epoxy c
Electronics Forum | Tue Oct 23 07:03:52 EDT 2007 | davef
We're not really sure. Usually when solder leaves the pads and wicks-up a component lead, it means the component lead is much warmer than the pad on the board. This is the direction we would have taken this if we hadn't taken the AgPd / conductive e
Electronics Forum | Tue Aug 30 09:24:08 EDT 2005 | Slaine
we manufacture a range of ceramic parts that have silver termination,there is already a small leaching problem (absorption of the termination by the solder in liquid form)with Sn62 that we live with, having to implement unleaded solder they are norma
Electronics Forum | Tue Aug 30 12:49:59 EDT 2005 | Ted
Slaine, We use a Pd/Ag thickfilm paste. Because of the leaching we had to start using solder pastes that have silver in it. For RoHS, we are using a solder paste with an alloy of Sn95/Ag05. We also have to double print the thickfilm pastes. I h
Electronics Forum | Fri Aug 13 16:54:20 EDT 2004 | davef
If the terminations on your components are not barrier plated, you must be very careful about the amount of time you stay above liquidous. As you'd expect, longer is not better. The longer you stay at liquidous, the more of the component terminatio
Electronics Forum | Thu Oct 18 18:39:15 EDT 2001 | davef
Responding to your questions ... RELIABILITY OF 1% SILVER SOLDER PASTE: It�s as good as the next solder paste, all other things the same. Look at your back articles by Jennie Hang in SMT magazine. I want to say she wrote an article on the topic i
Electronics Forum | Wed Aug 29 11:07:39 EDT 2007 | mikecollier
I am being asked to perform the same evaluation now with a Au/Pd termination varistor. We currently use a Pb/Sn process with an RMA flux. The manufacturer of the device recommends going to a 2% silver paste. What is the intended advantage with 2%
Electronics Forum | Thu Apr 19 16:54:32 EDT 2007 | flipit
I don't suggest using Pd/Ag or Ag/Pd terminated components unless you are forced to use them. You often see a line of demarcation that suggests a poorly wetted solder joint. I have had bad experiences with Pd/Ag terminated capacitors. Even when so
Electronics Forum | Thu Aug 12 20:32:44 EDT 2004 | usdigital
Indy, We use Palladium silver surface finish parts for silver epoxy attached parts only. It is our understanding that this finish is not for solder, but only silver epoxy attach. I expect that is you problem. Dave