Electronics Forum | Thu Apr 29 22:50:41 EDT 1999 | Kelly Morris
Tombstoning 0805s w/palladium/platinum/silver terminations We are experiencing tombstoning problems on 0805 packages that have paladium/platinum/silver terminations. It comes & goes...... I�ve checked the reflow profile, and paste deposition and a
Electronics Forum | Mon Mar 30 08:11:22 EST 1998 | Derek Drabenstadt
Does anyone have any experience with fired-silver/platinum/palladium lead terminations soldering. I have had issues on nickel over gold plated boards but not with HASL'd boards with tin/lead pads. Is this the norm?
Electronics Forum | Mon May 03 09:42:45 EDT 1999 | Mike McMonagle
| Tombstoning 0805s w/palladium/platinum/silver terminations | | We are experiencing tombstoning problems on 0805 packages that have paladium/platinum/silver terminations. It comes & goes...... | | I�ve checked the reflow profile, and paste deposi
Electronics Forum | Sun May 02 18:52:36 EDT 1999 | JohnW
| Tombstoning 0805s w/palladium/platinum/silver terminations | | We are experiencing tombstoning problems on 0805 packages that have paladium/platinum/silver terminations. It comes & goes...... | | I�ve checked the reflow profile, and paste deposi
Electronics Forum | Wed Apr 01 02:19:10 EST 1998 | Eldon Sanders
Yes, norm it is. Look back to February 98 discussion on this issue.
Electronics Forum | Thu Apr 02 08:26:36 EST 1998 | Steve Gregory
| Yes, norm it is. Look back to February 98 :discussion on this issue. Norm, That discussion does deal with palladium coated leads, but when I read your statement about silver/palladium fired terminations, I'm assuming that you're referring to
Electronics Forum | Fri Aug 13 16:54:20 EDT 2004 | davef
If the terminations on your components are not barrier plated, you must be very careful about the amount of time you stay above liquidous. As you'd expect, longer is not better. The longer you stay at liquidous, the more of the component terminatio
Electronics Forum | Thu Oct 18 18:39:15 EDT 2001 | davef
Responding to your questions ... RELIABILITY OF 1% SILVER SOLDER PASTE: It�s as good as the next solder paste, all other things the same. Look at your back articles by Jennie Hang in SMT magazine. I want to say she wrote an article on the topic i
Electronics Forum | Thu Aug 12 20:32:44 EDT 2004 | usdigital
Indy, We use Palladium silver surface finish parts for silver epoxy attached parts only. It is our understanding that this finish is not for solder, but only silver epoxy attach. I expect that is you problem. Dave
Electronics Forum | Sun Jul 04 19:49:05 EDT 2004 | indy
Hello Everyone, We are having some problem with Palladium-Silver surface finish. We have ceramic components with the above surface finish. When we try to assemble these on Sn/Pb solder, we are observing open joints. If we reflow the compt for more t